Cu3Sn-microporous copper composite joint for high-temperature die-attach applications

Purpose The purpose of this paper is to design a novel die-attach composite joint for high-temperature die-attach applications based on transient liquid phase bonding. Moreover, the microstructure, shear strength, electrical property, thermal conductivity and aging property of the composite joint were investigated. Design/methodology/approach The composite joint was made of microporous copper and Cu3Sn. Microporous copper was immersed into liquid Sn to achieve Sn-microporous copper composite structure for die attachment. By the thermo-compression bonding, the Cu3Sn-microporous copper composite joint with a thickness of 100 µm was successfully obtained after bonding at 350 °C for 5 min under a low pressure of 0.6 MPa. Findings After thermo-compression bonding, the resulting interconnection could withstand a high temperature of at most 676 °C, with the entire Sn transforming into Cu3Sn with high remelting temperatures. A large shear strength could be achieved with the Cu3Sn-microporous copper in the interconnections. The formed bondlines demonstrated a good electrical and thermal conductivity owing to the large existing amount of copper in the interconnections. Furthermore, the interconnection also exhibited excellent reliability under high temperature aging at 300 °C. Originality/value This die-attach composite joint was suitable for power devices operating under high temperatures or other harsh environments.