Influence of Bi additions on the distinct βSn grain structure of Sn-0.7Cu-0.05Ni-xBi (x = 0–4wt%)

Effects of Bi additions to Ag-containing lead-free solders have been the focus of a considerable amount of past investigation. However, the influence of Bi on Sn-Cu-Ni solders has not been studied extensively. In the present study, we explore the influence of Bi on microstructure formation of Sn-0.7Cu-0.05Ni/Cu solder joints both in the bulk and at the interface. It is shown that (i) Sn-0.7Cu-0.05Ni solidifies to produce a markedly different grain structure to Ag-containing lead-free alloys, with 5-8 independent βSn grains in each joint; (ii) Bi additions to Sn-0.7Cu-0.05Ni maintain this distinct βSn grain structure and had no discernible effect on the (Cu,Ni)6Sn5 interfacial intermetallic layers or primary intermetallic crystals.