High wet-etch resistance SiO2 films deposited by plasma-enhanced atomic layer deposition with 1,1,1-tris(dimethylamino)disilane

IF 2.4 3区 材料科学 Q3 MATERIALS SCIENCE, COATINGS & FILMS
S. Hwang, H. S. Kim, Dan N. Le, A. Sahota, Jaebeom Lee, Y. Jung, Sang Woo Kim, S. Kim, Rino Choi, Jinho Ahn, B. Hwang, Xiaobing Zhou, Jiyoung Kim
{"title":"High wet-etch resistance SiO2 films deposited by plasma-enhanced atomic layer deposition with 1,1,1-tris(dimethylamino)disilane","authors":"S. Hwang, H. S. Kim, Dan N. Le, A. Sahota, Jaebeom Lee, Y. Jung, Sang Woo Kim, S. Kim, Rino Choi, Jinho Ahn, B. Hwang, Xiaobing Zhou, Jiyoung Kim","doi":"10.1116/6.0001519","DOIUrl":null,"url":null,"abstract":"Figure 1. (a) Molecular structure of 1,1,1-tris(dimethylamino)disilane (TADS). The Si-Si bond can provide a higher molecular polarity and surface reactivity, which can be helpful for high-quality ALD SiO2 films. (b) In the temperature range of 115–390 C, TADS exhibits higher or at least comparable GPC in comparison with other aminosilane precursors. (c) The SiO2 films of TADS have not only high bulk film densities (< 2.38 g/cm at 390 C), which is higher than that (2.27 g/cm) of LPCVD SiO2 or close to that (2.4 g/cm ) of thermal oxide, but also high wet etch resistance with a WER of >1.6 nm/min in 200:1 HF.","PeriodicalId":17490,"journal":{"name":"Journal of Vacuum Science & Technology A","volume":"36 1","pages":""},"PeriodicalIF":2.4000,"publicationDate":"2022-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Vacuum Science & Technology A","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1116/6.0001519","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, COATINGS & FILMS","Score":null,"Total":0}
引用次数: 0

Abstract

Figure 1. (a) Molecular structure of 1,1,1-tris(dimethylamino)disilane (TADS). The Si-Si bond can provide a higher molecular polarity and surface reactivity, which can be helpful for high-quality ALD SiO2 films. (b) In the temperature range of 115–390 C, TADS exhibits higher or at least comparable GPC in comparison with other aminosilane precursors. (c) The SiO2 films of TADS have not only high bulk film densities (< 2.38 g/cm at 390 C), which is higher than that (2.27 g/cm) of LPCVD SiO2 or close to that (2.4 g/cm ) of thermal oxide, but also high wet etch resistance with a WER of >1.6 nm/min in 200:1 HF.
1,1,1-三(二甲氨基)二硅烷等离子体增强原子层沉积制备高耐湿蚀SiO2薄膜
图1所示。(a) 1,1,1-三(二甲氨基)二硅烷(TADS)的分子结构。Si-Si键可以提供更高的分子极性和表面反应性,这有助于制备高质量的ALD SiO2薄膜。(b)在115-390℃的温度范围内,与其他氨基硅烷前体相比,TADS表现出更高或至少相当的GPC。(c) TADS的SiO2薄膜不仅具有较高的体膜密度(390℃时< 2.38 g/cm),高于LPCVD SiO2 (2.27 g/cm)或接近热氧化SiO2 (2.4 g/cm),而且在200:1 HF时具有较高的耐湿蚀性,其WER >1.6 nm/min。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
Journal of Vacuum Science & Technology A
Journal of Vacuum Science & Technology A 工程技术-材料科学:膜
CiteScore
5.10
自引率
10.30%
发文量
247
审稿时长
2.1 months
期刊介绍: Journal of Vacuum Science & Technology A publishes reports of original research, letters, and review articles that focus on fundamental scientific understanding of interfaces, surfaces, plasmas and thin films and on using this understanding to advance the state-of-the-art in various technological applications.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信