Silicon Crack Root Cause Identification in a Wafer Level Chip Scale Package

Abstract

A different kind of challenge was encountered during the failure analysis (FA) of several customer-returned power devices. Determination of the failure mechanism (FM), silicon cratering or cracking, was straightforward; however, root cause process ownership identification was challenging. This paper presents the laborious analyses to identify the process that induced the failure.