Four-point flexural strength and microtensile bond strength of digitally and conventionally veneered zirconia

This study intended to evaluate the effect of digital veneering on four-point flexural strength (FS) and microtensile bond strength (μTBS) of veneered zirconia. Two different zirconia blocks, a lithium disilicate and a feldspathic ceramic block, and two different layering ceramics were used. IPS e.max Zir CAD (ZC) and Vita In-Ceram YZ (YZ) with yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) were used as substructures. IPS e.max CAD (LD), Vita Mark II (VMII), IPS e.max Ceram (EC) and Vita VM9 (VM9) were used for veneering. Resin cement and fusion ceramic were placed between veneer and zirconia substructure for digital veneering. A total of one hundred and fifty specimens in five groups (n = 30) were prepared for FS and tested in universal machine at 1.0 mm/min. One hundred specimens in five groups (n = 20) were obtained for the μTBS and tested at 1.0 mm/min. Statistical analysis was made by one way ANOVA and Tukey HSD. Conventional veneering showed statistically significant FS. ZC veneered with EC had the highest mean FS and the lowest was obtained in groups veneered through resin cement. YZ layered with VM9 had the highest mean μTBS. ZC veneered through fusion ceramic and YZ veneered through resin cement showed significantly lower and similar μTBS.