Inoculation Treatment of an Additively Manufactured 2024 Aluminium Alloy with Titanium Nanoparticles

Abstract Considerable studies on metal selective laser melting (SLM) have proved the necessity to refine microstructure parts fabricated by SLM in order to eliminate property anisotropy, hot-tearing and to increase the SLM-processability. In the present work, Ti nanoparticles, at the first time, were discovered to be an extremely effective inoculant for an SLMed 2024 aluminium alloy. 0.7 wt% addition of Ti nanoparticles was capable of substantially eliminating the hot-tearing cracks and columnar structure, and refining the grains in the SLMed 2024 alloy in a broad processing window. The substantial grain refinement in the Ti-inoculated 2024 alloy was attributed to the in-situ formation of Al3Ti nanoparticles with a L12 ordered structure, which formed a coherent interface with Al matrix and therefore significantly promoted the heterogeneous nucleation of the α-Al during solidification of melt pools in the SLM process. After a conventional T6 heat treatment, this SLMed alloy exhibited a superior balance of strength and ductility (tensile strength was up to 432 ± 20 MPa and elongation of 10 ± 0.8%), which was comparable to its wrought counterpart. This work can be considered as a breakthrough in research of fabricating high-strength aluminium alloys using SLM.