Thanapon Sinkruason, Anupong Luangpangai, N. Charoenthai, A. Rittidech, P. Pulphol, N. Vittayakorn, T. Bongkarn
{"title":"燃烧法制备SBNLT陶瓷的相形成及电学性能","authors":"Thanapon Sinkruason, Anupong Luangpangai, N. Charoenthai, A. Rittidech, P. Pulphol, N. Vittayakorn, T. Bongkarn","doi":"10.1080/02670836.2023.2238415","DOIUrl":null,"url":null,"abstract":"This report investigates the effect of firing temperatures on the phase formation, microstructure, electrical, and energy storage properties of lead-free Sr0.3(Bi0.7Na0.67Li0.03)0.5TiO3 (SBNLT) ceramics, synthesised by combustion technique. The samples were calcined between 700°C and 900°C for 2 h and sintered between 1100°C and 1200°C for 2 h. The ceramics exhibited coexisting rhombohedral and tetragonal phases, which were confirmed by the Rietveld refinement technique. A morphotropic phase boundary (MPB) of the rhombohedral and tetragonal phases, with a ratio of 49:51, was obtained at the sintering temperature of 1175°C. The highest maximum dielectric constant (ε max = 4667), polarisation (P max = 28.80 µC/cm2) and energy density (W = 0.95 J/cm3), with a breakdown strength of 70 kV/cm, were achieved from the sample sintered at 1175°C.","PeriodicalId":18232,"journal":{"name":"Materials Science and Technology","volume":"15 1","pages":""},"PeriodicalIF":1.7000,"publicationDate":"2023-07-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Phase formation and electrical properties of SBNLT ceramics prepared via combustion technique\",\"authors\":\"Thanapon Sinkruason, Anupong Luangpangai, N. Charoenthai, A. Rittidech, P. Pulphol, N. Vittayakorn, T. Bongkarn\",\"doi\":\"10.1080/02670836.2023.2238415\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This report investigates the effect of firing temperatures on the phase formation, microstructure, electrical, and energy storage properties of lead-free Sr0.3(Bi0.7Na0.67Li0.03)0.5TiO3 (SBNLT) ceramics, synthesised by combustion technique. The samples were calcined between 700°C and 900°C for 2 h and sintered between 1100°C and 1200°C for 2 h. The ceramics exhibited coexisting rhombohedral and tetragonal phases, which were confirmed by the Rietveld refinement technique. A morphotropic phase boundary (MPB) of the rhombohedral and tetragonal phases, with a ratio of 49:51, was obtained at the sintering temperature of 1175°C. The highest maximum dielectric constant (ε max = 4667), polarisation (P max = 28.80 µC/cm2) and energy density (W = 0.95 J/cm3), with a breakdown strength of 70 kV/cm, were achieved from the sample sintered at 1175°C.\",\"PeriodicalId\":18232,\"journal\":{\"name\":\"Materials Science and Technology\",\"volume\":\"15 1\",\"pages\":\"\"},\"PeriodicalIF\":1.7000,\"publicationDate\":\"2023-07-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Science and Technology\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1080/02670836.2023.2238415\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science and Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/02670836.2023.2238415","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Phase formation and electrical properties of SBNLT ceramics prepared via combustion technique
This report investigates the effect of firing temperatures on the phase formation, microstructure, electrical, and energy storage properties of lead-free Sr0.3(Bi0.7Na0.67Li0.03)0.5TiO3 (SBNLT) ceramics, synthesised by combustion technique. The samples were calcined between 700°C and 900°C for 2 h and sintered between 1100°C and 1200°C for 2 h. The ceramics exhibited coexisting rhombohedral and tetragonal phases, which were confirmed by the Rietveld refinement technique. A morphotropic phase boundary (MPB) of the rhombohedral and tetragonal phases, with a ratio of 49:51, was obtained at the sintering temperature of 1175°C. The highest maximum dielectric constant (ε max = 4667), polarisation (P max = 28.80 µC/cm2) and energy density (W = 0.95 J/cm3), with a breakdown strength of 70 kV/cm, were achieved from the sample sintered at 1175°C.
期刊介绍:
《Materials Science and Technology》(MST) is an international forum for the publication of refereed contributions covering fundamental and technological aspects of materials science and engineering.