LiCoO2 Cathode Material Prepared through Two Step Sintering Process

LiCoO2 cathode material has been continuously applied in commercial LIBs cells. It has high gravimetric and volumetric density. In this research, an economical approach to obtain LiCoO2 is proposed. Pure cobalt oxide (Co3O4) precursor was obtained via atmospheric precipitation of cobalt sulfate and thermal decomposition of the as-obtained hydroxide precursor. The next heat treatment was performed to obtain LiCoO2 powder. To investigate the characteristic of the precursor and the final product, XRD, FTIR, and SEM analysis were conducted. The final product has hexagonal structure and quasi spherical morphology. The size of the particle is in micron. The charge-discharge analysis of LiCoO2 was conducted in LiCoO2/Graphite system where the initial capacity of LiCoO2 is 120 mAh/g at the current density of 0.1 C (20 mA/g). Overall, this method can be used for large scale LiCoO­2 cell production.