Lucas Miguel Candido, Eduardo Bellini Ferreira, Lígia Antunes Pereira Pinelli
{"title":"研磨和再生热处理对氧化锆/瓷贴面界面抗断裂性的影响","authors":"Lucas Miguel Candido, Eduardo Bellini Ferreira, Lígia Antunes Pereira Pinelli","doi":"10.3290/j.jad.b2701695","DOIUrl":null,"url":null,"abstract":"<p><strong>Purpose: </strong>To experimentally assess the effect of regenerative heat treatment (HT) on yttria-stabilized tetragonal zirconia polycrystalline ceramic (Y-TZP) to guarantee veneer adhesion strength.</p><p><strong>Materials and methods: </strong>One surface of bar-shaped Y-TZP specimens was ground (G) with a diamond stone, while the control samples (C) were not. Groups C900 and G900 were submitted to HT at 900°C for 60 min, whereas groups C1000 and G1000 were submitted to HT at 1000°C for 30 min. The treated surfaces were characterized by x-ray diffractometry (XRD), scanning electron microscopy (SEM), and optical and mechanical profilometry. The energy release rate through interface fracture was determined by a four-point bending test on notched Y-TZP veneered specimens. XRD was refined by the Rietveld method, mean roughness (Ra) and energy release rate were submitted to two-way ANOVA (a = 0.05), and the images were analyzed descriptively.</p><p><strong>Results: </strong>The monoclinic phase (vol%), means of Ra (µm), and the energy release rate (J/m2) were, respectively: C = 1.2/0.17/6.8, C900 = 0.0/0.18/6.6, C1000 = 0.0/0.18/7.6, G = 2.6/1.16/8.3, G900 = 0.0/1.07/8.0, and G1000 = 0.0/1.01/5.7. The surface fraction of monoclinic zirconia increased by grinding and decreased by HT. Ra also increased after grinding (p < 0.005) but remained unaltered after HT (p = 0.22). Increased irregularity was observed in the G groups and a subtle smoothing of the surface after HT. After the fracture of the bilayers, a residual amount of porcelain could be seen on the zirconia surface in all groups. The energy release rate was statistically equal among all groups (p > 0.05).</p><p><strong>Conclusion: </strong>Heat treatment after grinding completely restored the tetragonal phase of zirconia without altering the energy release rate during interfacial fracture.</p>","PeriodicalId":94234,"journal":{"name":"The journal of adhesive dentistry","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2022-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Grinding and Regenerative Heat Treatment on the Fracture Resistance of a Zirconia/Porcelain Veneer Interface.\",\"authors\":\"Lucas Miguel Candido, Eduardo Bellini Ferreira, Lígia Antunes Pereira Pinelli\",\"doi\":\"10.3290/j.jad.b2701695\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Purpose: </strong>To experimentally assess the effect of regenerative heat treatment (HT) on yttria-stabilized tetragonal zirconia polycrystalline ceramic (Y-TZP) to guarantee veneer adhesion strength.</p><p><strong>Materials and methods: </strong>One surface of bar-shaped Y-TZP specimens was ground (G) with a diamond stone, while the control samples (C) were not. Groups C900 and G900 were submitted to HT at 900°C for 60 min, whereas groups C1000 and G1000 were submitted to HT at 1000°C for 30 min. The treated surfaces were characterized by x-ray diffractometry (XRD), scanning electron microscopy (SEM), and optical and mechanical profilometry. The energy release rate through interface fracture was determined by a four-point bending test on notched Y-TZP veneered specimens. XRD was refined by the Rietveld method, mean roughness (Ra) and energy release rate were submitted to two-way ANOVA (a = 0.05), and the images were analyzed descriptively.</p><p><strong>Results: </strong>The monoclinic phase (vol%), means of Ra (µm), and the energy release rate (J/m2) were, respectively: C = 1.2/0.17/6.8, C900 = 0.0/0.18/6.6, C1000 = 0.0/0.18/7.6, G = 2.6/1.16/8.3, G900 = 0.0/1.07/8.0, and G1000 = 0.0/1.01/5.7. The surface fraction of monoclinic zirconia increased by grinding and decreased by HT. Ra also increased after grinding (p < 0.005) but remained unaltered after HT (p = 0.22). Increased irregularity was observed in the G groups and a subtle smoothing of the surface after HT. After the fracture of the bilayers, a residual amount of porcelain could be seen on the zirconia surface in all groups. The energy release rate was statistically equal among all groups (p > 0.05).</p><p><strong>Conclusion: </strong>Heat treatment after grinding completely restored the tetragonal phase of zirconia without altering the energy release rate during interfacial fracture.</p>\",\"PeriodicalId\":94234,\"journal\":{\"name\":\"The journal of adhesive dentistry\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2022-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"The journal of adhesive dentistry\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.3290/j.jad.b2701695\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"The journal of adhesive dentistry","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.3290/j.jad.b2701695","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Effect of Grinding and Regenerative Heat Treatment on the Fracture Resistance of a Zirconia/Porcelain Veneer Interface.
Purpose: To experimentally assess the effect of regenerative heat treatment (HT) on yttria-stabilized tetragonal zirconia polycrystalline ceramic (Y-TZP) to guarantee veneer adhesion strength.
Materials and methods: One surface of bar-shaped Y-TZP specimens was ground (G) with a diamond stone, while the control samples (C) were not. Groups C900 and G900 were submitted to HT at 900°C for 60 min, whereas groups C1000 and G1000 were submitted to HT at 1000°C for 30 min. The treated surfaces were characterized by x-ray diffractometry (XRD), scanning electron microscopy (SEM), and optical and mechanical profilometry. The energy release rate through interface fracture was determined by a four-point bending test on notched Y-TZP veneered specimens. XRD was refined by the Rietveld method, mean roughness (Ra) and energy release rate were submitted to two-way ANOVA (a = 0.05), and the images were analyzed descriptively.
Results: The monoclinic phase (vol%), means of Ra (µm), and the energy release rate (J/m2) were, respectively: C = 1.2/0.17/6.8, C900 = 0.0/0.18/6.6, C1000 = 0.0/0.18/7.6, G = 2.6/1.16/8.3, G900 = 0.0/1.07/8.0, and G1000 = 0.0/1.01/5.7. The surface fraction of monoclinic zirconia increased by grinding and decreased by HT. Ra also increased after grinding (p < 0.005) but remained unaltered after HT (p = 0.22). Increased irregularity was observed in the G groups and a subtle smoothing of the surface after HT. After the fracture of the bilayers, a residual amount of porcelain could be seen on the zirconia surface in all groups. The energy release rate was statistically equal among all groups (p > 0.05).
Conclusion: Heat treatment after grinding completely restored the tetragonal phase of zirconia without altering the energy release rate during interfacial fracture.