Stacked 1/3 Tubular Plates for Fixation of Pediatric Forearm Fractures: A Biomechanical Study

Introduction Among operatively treated pediatric forearm fractures, many different fixation constructs are described. The goal of this study was to define the biomechanical properties of a double stacked 1/3 tubular plate construct used by the senior author for some fractures and to review available literature regarding the use of stacked plates. Methods Biomechanical testing was performed by 4-point bending of three different plate constructs: 1/3 tubular plate, stacked 1/3 tubular plates, and 2.7 mm LC-DCP plate. Five test specimens were evaluated for each of the three plate constructs. From stress-strain curves, flexural stiffness (N/mm), force to cause plastic deformation (N), and force to cause 10° bend (N) were calculated and compared using standard t-test statistics. Results Key outcome parameter means (± SD) for the three plate constructs (1/3 tubular plate, stacked 1/3 tubular plates, and 2.7 mm LC-DCP plate) were reported respectively as follows: flexural stiffness (55.4 ± 3.5 N/mm, 131.7 ± 3.5 N/mm, 113.3 ± 12.1 N/mm), force to cause plastic deformation (113.6 ± 11.0 N, 242.1 ± 13.0 N, 192.2 ± 17.9 N), and force to cause a 10° bend (140.0 ± 8.4 N, 299.4 ± 14.1 N, 265.5 ± 21.2 N). Mean values of all three measures were significantly larger for the stacked 1/3 tubular plates than for the other plate constructs. Conclusions The stacked 1/3 tubular plate construct was biomechanically superior to the other plate constructs tested. Stacked plating significantly improved stiffness of the fracture fixation construct supporting the use of this technique in selected trauma cases.