Band Gap Energy and Lattice Distortion in Anatase TiO2 Thin Films Prepared by Reactive Sputtering with Different Thicknesses.

TiO₂ is an abundant material on Earth, essential for the sustainable and cost-effective development of various technologies, with anatase being the most effective polymorph for photocatalytic and photovoltaic applications. Bulk crystalline anatase TiO₂ exhibits a band gap energy E_gA = 3.2 eV, for tetragonal lattice parameters a_A = 0.3785 nm and c_A = 0.9514 nm, but these characteristics vary for amorphous or polycrystalline thin films. Reactive magnetron sputtering has proven suitable for the preparation of TiO₂ coatings on glass fiber substrates, with structural and optical characteristics that change during growth. Below a minimum thickness (t < 0.2 μm), the films have an amorphous nature or extremely small crystallite sizes not observable by X-ray diffraction. Afterwards, compressed quasi-randomly orientated crystallites are detected (volume strain ΔV = -0.02 and stress σ_V = -3.5 GPa for t = 0.2 μm) that evolve into relaxed and preferentially (004) orientated crystallites, reaching the standard anatase values at t ~ 1.4 μm with σ_V = 0.0 GPa. The band gap energy increases with lattice distortion according to the relation ∆E_g (eV) = -6∆V, and a further increase is observed for the thinnest coatings (∆E_g = 0.24 eV for t = 0.05 μm).