{"title":"修正：用氟单体和交联单体改性聚偏二氯乙烯树脂。","authors":"","doi":"10.1002/marc.202500356","DOIUrl":null,"url":null,"abstract":"<p>Correction for ‘Modifying Polyvinylidene Chloride Resin with Fluorine Monomer and Cross-Linking Monomers’ by Fengjun Gao et al., <i>Macromol. Rapid Commun</i>. <b>2024</b>, <i>45</i>, 2400402, https://doi.org/10.1002/marc.202400402.</p><p>Parts of the data presented in Figures 7 and 8 are incorrect. The authors have checked the recorded experimental results carefully and provided replacement data for FT1.5 in Figure 7; and F15b in Figure 8. Meanwhile, the result of the interior region is added in Figure 8 as F15c. This correction does not alter the conclusions presented in this <i>Macromolecular Rapid Communications</i> paper.</p><p>1) The correct Figure 7 is presented as following:</p><p>2) The correct Figure 8 is presented as following:</p><p>The sentence on page 6 “The FTIR spectrum of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15), which was because no special groups were introduced in the added crosslinking monomer.” should be corrected as “The characteristic absorption peak at 2915 cm<sup>−1</sup> of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15). This indicates that TMPTMA has been incorporated into the PVDC resin through the synthesis reaction.”</p><p>The sentence on page 6 “The unsaturated carbon C─H stretching vibrational interval at 3000–3100 cm<sup>−1</sup> and the C═C double bond stretching vibrational interval at 1620–1680 cm<sup>−1</sup> do not change,” should be corrected as “Moreover, the C═C double bond stretching vibrational interval at 1620–1680 cm<sup>−1</sup> does not change,”</p><p>The sentence on page 6 “In addition, the fluorine and carbon contents of F15a are higher than F15b,” should be corrected to “In addition, the fluorine and carbon contents on the bottom surface (F15a) and top surface (F15b) are higher than those in the interior region (F15c) of the sample,”</p><p>The authors appreciate the support from the readers, editors, and publishers. Meanwhile, the authors apologize for the confusion caused by this mistake.</p>","PeriodicalId":205,"journal":{"name":"Macromolecular Rapid Communications","volume":"46 15","pages":""},"PeriodicalIF":4.3000,"publicationDate":"2025-05-21","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://onlinelibrary.wiley.com/doi/epdf/10.1002/marc.202500356","citationCount":"0","resultStr":"{\"title\":\"Correction: Modifying Polyvinylidene Chloride Resin with Fluorine Monomer and Cross-Linking Monomers\",\"authors\":\"\",\"doi\":\"10.1002/marc.202500356\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>Correction for ‘Modifying Polyvinylidene Chloride Resin with Fluorine Monomer and Cross-Linking Monomers’ by Fengjun Gao et al., <i>Macromol. Rapid Commun</i>. <b>2024</b>, <i>45</i>, 2400402, https://doi.org/10.1002/marc.202400402.</p><p>Parts of the data presented in Figures 7 and 8 are incorrect. The authors have checked the recorded experimental results carefully and provided replacement data for FT1.5 in Figure 7; and F15b in Figure 8. Meanwhile, the result of the interior region is added in Figure 8 as F15c. This correction does not alter the conclusions presented in this <i>Macromolecular Rapid Communications</i> paper.</p><p>1) The correct Figure 7 is presented as following:</p><p>2) The correct Figure 8 is presented as following:</p><p>The sentence on page 6 “The FTIR spectrum of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15), which was because no special groups were introduced in the added crosslinking monomer.” should be corrected as “The characteristic absorption peak at 2915 cm<sup>−1</sup> of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15). This indicates that TMPTMA has been incorporated into the PVDC resin through the synthesis reaction.”</p><p>The sentence on page 6 “The unsaturated carbon C─H stretching vibrational interval at 3000–3100 cm<sup>−1</sup> and the C═C double bond stretching vibrational interval at 1620–1680 cm<sup>−1</sup> do not change,” should be corrected as “Moreover, the C═C double bond stretching vibrational interval at 1620–1680 cm<sup>−1</sup> does not change,”</p><p>The sentence on page 6 “In addition, the fluorine and carbon contents of F15a are higher than F15b,” should be corrected to “In addition, the fluorine and carbon contents on the bottom surface (F15a) and top surface (F15b) are higher than those in the interior region (F15c) of the sample,”</p><p>The authors appreciate the support from the readers, editors, and publishers. Meanwhile, the authors apologize for the confusion caused by this mistake.</p>\",\"PeriodicalId\":205,\"journal\":{\"name\":\"Macromolecular Rapid Communications\",\"volume\":\"46 15\",\"pages\":\"\"},\"PeriodicalIF\":4.3000,\"publicationDate\":\"2025-05-21\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://onlinelibrary.wiley.com/doi/epdf/10.1002/marc.202500356\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Macromolecular Rapid Communications\",\"FirstCategoryId\":\"92\",\"ListUrlMain\":\"https://onlinelibrary.wiley.com/doi/10.1002/marc.202500356\",\"RegionNum\":3,\"RegionCategory\":\"化学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"POLYMER SCIENCE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Macromolecular Rapid Communications","FirstCategoryId":"92","ListUrlMain":"https://onlinelibrary.wiley.com/doi/10.1002/marc.202500356","RegionNum":3,"RegionCategory":"化学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"POLYMER SCIENCE","Score":null,"Total":0}
Correction: Modifying Polyvinylidene Chloride Resin with Fluorine Monomer and Cross-Linking Monomers
Correction for ‘Modifying Polyvinylidene Chloride Resin with Fluorine Monomer and Cross-Linking Monomers’ by Fengjun Gao et al., Macromol. Rapid Commun. 2024, 45, 2400402, https://doi.org/10.1002/marc.202400402.
Parts of the data presented in Figures 7 and 8 are incorrect. The authors have checked the recorded experimental results carefully and provided replacement data for FT1.5 in Figure 7; and F15b in Figure 8. Meanwhile, the result of the interior region is added in Figure 8 as F15c. This correction does not alter the conclusions presented in this Macromolecular Rapid Communications paper.
1) The correct Figure 7 is presented as following:
2) The correct Figure 8 is presented as following:
The sentence on page 6 “The FTIR spectrum of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15), which was because no special groups were introduced in the added crosslinking monomer.” should be corrected as “The characteristic absorption peak at 2915 cm−1 of the resin modified with TMPTMA (FT1.5) did not change significantly compared with that of the fluorine-modified resin (F15). This indicates that TMPTMA has been incorporated into the PVDC resin through the synthesis reaction.”
The sentence on page 6 “The unsaturated carbon C─H stretching vibrational interval at 3000–3100 cm−1 and the C═C double bond stretching vibrational interval at 1620–1680 cm−1 do not change,” should be corrected as “Moreover, the C═C double bond stretching vibrational interval at 1620–1680 cm−1 does not change,”
The sentence on page 6 “In addition, the fluorine and carbon contents of F15a are higher than F15b,” should be corrected to “In addition, the fluorine and carbon contents on the bottom surface (F15a) and top surface (F15b) are higher than those in the interior region (F15c) of the sample,”
The authors appreciate the support from the readers, editors, and publishers. Meanwhile, the authors apologize for the confusion caused by this mistake.