Effects of Detox Juices on Color Stability and Surface Roughness of Universal Chromatic Resin Composites.

This study investigated the color stability and surface roughness of universal chromatic resin-based composites (RBCs) after immersion in detox juices. One hundred seventy-six disc-shaped specimens (8 mm in diameter and 2 mm in thickness) were prepared using four universal chromatic RBCs: NeoSpectra ST (NS), Omnichroma (OM), Charisma Topaz One (CO), and G-ænial Universal Injectable (GI). Specimens of each material were randomly divided into four subgroups (n=11) and immersed in either the assigned detox juices (red, green, or yellow) or distilled water (control). Color and surface roughness measurements were taken at baseline, 15 and 30 days of immersion. Scanning electron microscopy (SEM) was used to evaluate the surface topography of the composites. The color change [CIEDE2000 (ΔE00)] and surface roughness (Ra) values were analyzed using generalized linear models and multiple comparison tests with Bonferroni correction. Correlation analysis was performed using Spearman rank correlation test. The main variable effects of "composite and immersion media" were significant for both color change and surface roughness parameters (p<0.001). Additionally, the main effect of the "evaluation period" was significant only for surface roughness (p=0.001). The highest discoloration occurred in the GI group immersed in a red beverage, while the CO group immersed in yellow beverage had the highest Ra values. In SEM analysis, OM demonstrated a more homogeneous filler structure with clearly visible nano-spherical fillers and nanoclusters, contributing to its superior smoothness. Conversely, a significant increase in rough areas was observed, especially in NS exposed to the green beverage and CO exposed to the yellow beverage, after 30 days. While the immersion of resin composites in detox juices induced an acceptable color alteration except for OM and GI groups immersed in the red beverage, all tested materials exhibited clinically admissible results regarding surface roughness.