Effective adsorption of Cr(VI) from aqueous solution by Mg-Fe LDH supported on orange peel activated carbon: isotherm, kinetic, thermodynamics and mechanism studies.

The toxic Cr(VI) contaminating water released from the metallurgical, dyeing, and electroplating industries is getting worse day by day and is extremely hazardous to human health. Thus, the development of a cost-effective, quick, and efficient adsorbent is highly essential for the Cr(VI) decontamination from wastewater. Herein, a microwave-assisted carbon-based composite called Mg-Fe LDH@OPAC was prepared by assembling Mg-Fe LDH onto orange peel-activated carbon (OAPC). Prior to investigating deeply into the adsorption behavior of the composite, the Mg-Fe LDH@OPAC formation was confirmed by using instrumental techniques like FESEM, EDS, Zeta potential, XRD, FTIR, Raman, XPS, and BET analyzer. The material had a high surface area of 143.9 m²/g and showed a good monolayer Langmuir uptake capacity of 118.36 mg/g. Under ideal circumstances, the maximum amount of Cr(VI) was removed within just 120 min and showed high efficiency in the presence of other coexisting anions respectively. The adsorption was accounted by pseudo-second-order kinetics and spontaneous in nature. Ultimately, a possible adsorption mechanism was suggested, confirmed by XPS studies; which showed that oxidation-reduction, electrostatic interaction, and surface complexation reaction were responsible for Cr(VI) adsorption on Mg-Fe LDH@OPAC surface.