Layer-by-layer assembling boron nitride/polyethyleneimine/MXene hierarchical sandwich structure onto basalt fibers for high-performance epoxy composites

Interfacial adhesion directly affects the mechanical properties of basalt fiber (BF)-reinforced polymer composites. To construct a more superior interphase between BFs and epoxy resin (EP) than a weak interphase of the unmodified BF/EP, we propose a hierarchical sandwich structure consisting of sodium hydroxide–activated boron nitride (BN_OH), polyethyleneimine (PEI), and MXene (MX, Ti₃C₂T_x) through facile layer-by-layer self-assembly. The fabricated BN_OH/P/MX sandwich structure (P denoting “PEI”) can synergistically improve the interface adhesion by enhancing the mechanical interlocking and chemical bonding of the composites. When the composites reinforced by BF–BN_OH/P/MX subject to the external loading, flexible PEI molecules allow two-dimensional (2D) rigid BN_OH and MX nanosheets to slip at the interface by uncurling the molecular chains, dissipating a great amount of energy during the fracture progress. Meanwhile, the hierarchical BN_OH/P/MX sandwich structure acts as an excellent interface and possesses multistage gradient modulus and wider thickness, uniformly and efficiently transferring the stress from the EP matrix to BFs. The interfacial shear strength, impact strength, and fracture toughness of BF–BN_OH/P/MX-reinforced EP composite are substantially improved by 45.9 %, 60.6 %, and 148.9 %, respectively, compared with bare BF–based composites. This study can provide valuable references and inspirations for designing and constructing high-quality interfaces for high-strength and high-toughness BF structural materials, taking advantage of 2D materials.