Multi-Wavelength Excitable Multicolor Upconversion and Ratiometric Luminescence Thermometry of Yb3+/Er3+ Co-Doped NaYGeO4 Microcrystals.

Excitation wavelength controllable lanthanide upconversion allows for real-time manipulation of luminescent color in a composition-fixed material, which has been proven to be conducive to a variety of applications, such as optical anti-counterfeiting and information security. However, current available materials highly rely on the elaborate core-shell structure in order to ensure efficient excitation-dependent energy transfer routes. Herein, multicolor upconversion luminescence in response to both near-infrared I and near-infrared II (NIR-I and NIR-II) excitations is realized in a novel but simple NaYGeO₄:Yb³⁺/Er³⁺ phosphor. The remarkably enhanced red emission ratio under 1532 nm excitation, compared with that under 980 nm excitation, could be attributed to the Yb³⁺-mediated cross-relaxation energy transfers. Moreover, multi-wavelength excitable temperature-dependent (295-823 K) upconversion luminescence realizes a ratiometric thermometry relying on the thermally coupled levels (TCLs) of Er³⁺. Detailed investigations demonstrate that changing excitation wavelength makes little difference for the performances of TCL-based ratiometric thermometry of NaYGeO₄:Yb³⁺/Er³⁺. These findings gain more insights to manipulate cross-relaxations for excitation controllable upconversion in single activator doped materials and benefit the cognition of the effect of excitation wavelength on ratiometric luminescence thermometry.