通过简单的两步程序加入还原氧化石墨烯,增强 LiFePO4 阴极材料的性能

IF 4.3 3区 材料科学 Q2 CHEMISTRY, MULTIDISCIPLINARY
M.P. Quiroga Argañaraz , K. Jori , J.M. Ramallo-López , A. Visintin , F.G. Requejo , M.G. Ortiz
{"title":"通过简单的两步程序加入还原氧化石墨烯,增强 LiFePO4 阴极材料的性能","authors":"M.P. Quiroga Argañaraz ,&nbsp;K. Jori ,&nbsp;J.M. Ramallo-López ,&nbsp;A. Visintin ,&nbsp;F.G. Requejo ,&nbsp;M.G. Ortiz","doi":"10.1016/j.jpcs.2024.112353","DOIUrl":null,"url":null,"abstract":"<div><div>The aim of the present work is the improvement of LiFePO<sub>4</sub> (LFP) as cathodic material for Lithium Batteries (LIBs) by controlled incorporation of graphene oxide (GO) and its subsequent reduction during LFP synthesis. The electrochemical performance of the samples is analysed after reduction treatment of GO in different steps of the synthesis. The purpose of the reduction is to provide LFP particles with higher conductivity through a uniform conductive carbon coating that facilitates the migration of Li<sup>+</sup> ions in the cathode for charge-discharge process. These electrochemical measurements revealed an initial discharge capacity of 70.19 mAh g<sup>−1</sup> for LFP without GO, 141.3 mAh g<sup>−1</sup> and 154.3 mAh g<sup>−1</sup> with GO added in heat-treatment and solvothermal step, at 0.5C rate, respectively. Additionally, the cycling stability of the samples with GO improves the corresponding one obtained for pristine LFP. At 0.5C rate cycle-life, the LFP with GO combined with raw materials during solvothermal synthesis, attained capacity retention of 99 % after 100 cycles, decreasing to values of 88 % and 87 % for LFP with GO incorporated just before thermal treatment and LFP without GO. These results indicate that the LFP with GO incorporated initially in the synthesis improves rate capability of the material, reaching reversible capacity of 158.5 mAh g<sup>−1</sup> at 0.1C, 154.4 mAh g<sup>−1</sup> at 0.2C, 151.3 mAh g<sup>−1</sup> at 0.5C, 122.7 mAh g<sup>−1</sup> at 1C and 112.6 mAh g<sup>−1</sup> at 2C. The improvement in electrochemical behaviour can be attributed to the optimization of the synthesis process that provides a well-crosslinked interior of the composite and, therefore, a stable conductive network which has an associated higher diffusion coefficient.</div></div>","PeriodicalId":16811,"journal":{"name":"Journal of Physics and Chemistry of Solids","volume":"196 ","pages":"Article 112353"},"PeriodicalIF":4.3000,"publicationDate":"2024-09-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Enhancement of LiFePO4 cathodic material through incorporation of reduced graphene oxide via a simple two-step procedure\",\"authors\":\"M.P. Quiroga Argañaraz ,&nbsp;K. Jori ,&nbsp;J.M. Ramallo-López ,&nbsp;A. Visintin ,&nbsp;F.G. Requejo ,&nbsp;M.G. Ortiz\",\"doi\":\"10.1016/j.jpcs.2024.112353\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><div>The aim of the present work is the improvement of LiFePO<sub>4</sub> (LFP) as cathodic material for Lithium Batteries (LIBs) by controlled incorporation of graphene oxide (GO) and its subsequent reduction during LFP synthesis. The electrochemical performance of the samples is analysed after reduction treatment of GO in different steps of the synthesis. The purpose of the reduction is to provide LFP particles with higher conductivity through a uniform conductive carbon coating that facilitates the migration of Li<sup>+</sup> ions in the cathode for charge-discharge process. These electrochemical measurements revealed an initial discharge capacity of 70.19 mAh g<sup>−1</sup> for LFP without GO, 141.3 mAh g<sup>−1</sup> and 154.3 mAh g<sup>−1</sup> with GO added in heat-treatment and solvothermal step, at 0.5C rate, respectively. Additionally, the cycling stability of the samples with GO improves the corresponding one obtained for pristine LFP. At 0.5C rate cycle-life, the LFP with GO combined with raw materials during solvothermal synthesis, attained capacity retention of 99 % after 100 cycles, decreasing to values of 88 % and 87 % for LFP with GO incorporated just before thermal treatment and LFP without GO. These results indicate that the LFP with GO incorporated initially in the synthesis improves rate capability of the material, reaching reversible capacity of 158.5 mAh g<sup>−1</sup> at 0.1C, 154.4 mAh g<sup>−1</sup> at 0.2C, 151.3 mAh g<sup>−1</sup> at 0.5C, 122.7 mAh g<sup>−1</sup> at 1C and 112.6 mAh g<sup>−1</sup> at 2C. The improvement in electrochemical behaviour can be attributed to the optimization of the synthesis process that provides a well-crosslinked interior of the composite and, therefore, a stable conductive network which has an associated higher diffusion coefficient.</div></div>\",\"PeriodicalId\":16811,\"journal\":{\"name\":\"Journal of Physics and Chemistry of Solids\",\"volume\":\"196 \",\"pages\":\"Article 112353\"},\"PeriodicalIF\":4.3000,\"publicationDate\":\"2024-09-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Physics and Chemistry of Solids\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0022369724004888\",\"RegionNum\":3,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Physics and Chemistry of Solids","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0022369724004888","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

摘要

本研究的目的是通过控制氧化石墨烯(GO)的加入以及随后在 LFP 合成过程中对其进行还原处理,改进作为锂电池(LIB)阴极材料的 LiFePO4(LFP)。在合成的不同步骤中对 GO 进行还原处理后,对样品的电化学性能进行了分析。还原处理的目的是通过均匀的导电碳涂层使 LFP 颗粒具有更高的导电性,从而促进 Li+ 离子在阴极中的迁移,实现充放电过程。这些电化学测量结果表明,在 0.5C 速率下,不添加 GO 的 LFP 初始放电容量为 70.19 mAh g-1,添加 GO 的 LFP 初始放电容量为 141.3 mAh g-1 和 154.3 mAh g-1。此外,添加了 GO 的样品的循环稳定性比原始 LFP 的相应稳定性更高。在 0.5 摄氏度的循环寿命下,溶解热合成过程中添加了 GO 的 LFP 与原材料结合,在 100 次循环后的容量保持率达到 99%,而在热处理前添加了 GO 的 LFP 和未添加 GO 的 LFP 的容量保持率分别为 88% 和 87%。这些结果表明,在合成初期加入 GO 的 LFP 提高了材料的速率能力,其可逆容量在 0.1C 时达到 158.5 mAh g-1,0.2C 时达到 154.4 mAh g-1,0.5C 时达到 151.3 mAh g-1,1C 时达到 122.7 mAh g-1,2C 时达到 112.6 mAh g-1。电化学性能的改善可归功于合成工艺的优化,它使复合材料的内部交联良好,从而形成了稳定的导电网络,并相应提高了扩散系数。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

Enhancement of LiFePO4 cathodic material through incorporation of reduced graphene oxide via a simple two-step procedure

Enhancement of LiFePO4 cathodic material through incorporation of reduced graphene oxide via a simple two-step procedure
The aim of the present work is the improvement of LiFePO4 (LFP) as cathodic material for Lithium Batteries (LIBs) by controlled incorporation of graphene oxide (GO) and its subsequent reduction during LFP synthesis. The electrochemical performance of the samples is analysed after reduction treatment of GO in different steps of the synthesis. The purpose of the reduction is to provide LFP particles with higher conductivity through a uniform conductive carbon coating that facilitates the migration of Li+ ions in the cathode for charge-discharge process. These electrochemical measurements revealed an initial discharge capacity of 70.19 mAh g−1 for LFP without GO, 141.3 mAh g−1 and 154.3 mAh g−1 with GO added in heat-treatment and solvothermal step, at 0.5C rate, respectively. Additionally, the cycling stability of the samples with GO improves the corresponding one obtained for pristine LFP. At 0.5C rate cycle-life, the LFP with GO combined with raw materials during solvothermal synthesis, attained capacity retention of 99 % after 100 cycles, decreasing to values of 88 % and 87 % for LFP with GO incorporated just before thermal treatment and LFP without GO. These results indicate that the LFP with GO incorporated initially in the synthesis improves rate capability of the material, reaching reversible capacity of 158.5 mAh g−1 at 0.1C, 154.4 mAh g−1 at 0.2C, 151.3 mAh g−1 at 0.5C, 122.7 mAh g−1 at 1C and 112.6 mAh g−1 at 2C. The improvement in electrochemical behaviour can be attributed to the optimization of the synthesis process that provides a well-crosslinked interior of the composite and, therefore, a stable conductive network which has an associated higher diffusion coefficient.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Journal of Physics and Chemistry of Solids
Journal of Physics and Chemistry of Solids 工程技术-化学综合
CiteScore
7.80
自引率
2.50%
发文量
605
审稿时长
40 days
期刊介绍: The Journal of Physics and Chemistry of Solids is a well-established international medium for publication of archival research in condensed matter and materials sciences. Areas of interest broadly include experimental and theoretical research on electronic, magnetic, spectroscopic and structural properties as well as the statistical mechanics and thermodynamics of materials. The focus is on gaining physical and chemical insight into the properties and potential applications of condensed matter systems. Within the broad scope of the journal, beyond regular contributions, the editors have identified submissions in the following areas of physics and chemistry of solids to be of special current interest to the journal: Low-dimensional systems Exotic states of quantum electron matter including topological phases Energy conversion and storage Interfaces, nanoparticles and catalysts.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信