用于保护 T2 相钼合金的抗氧化 Mo30Si60B10 涂层

IF 2.9 Q1 MATERIALS SCIENCE, CERAMICS

Open Ceramics Pub Date : 2024-09-10 DOI:10.1016/j.oceram.2024.100671

A.D. Chertova , A. Yu. Potanin , P. Feng , X. Ren , E.A. Levashov , Ph. V. Kiryukhantsev-Korneev

{"title":"用于保护 T2 相钼合金的抗氧化 Mo30Si60B10 涂层","authors":"A.D. Chertova , A. Yu. Potanin , P. Feng , X. Ren , E.A. Levashov , Ph. V. Kiryukhantsev-Korneev","doi":"10.1016/j.oceram.2024.100671","DOIUrl":null,"url":null,"abstract":"<div><div>This study focuses on fabrication of a Mo30Si60B10 coating with elevated silicon content, which enhances working properties of Mo-alloy based on the Т2 phase (t-Mo5SiB2). The Mo30Si60B10 coating has a columnar structure. The alloy is characterized by hardness of 17 GPa; Young's modulus of 304 GPa, and elastic recovery of 29 %. Deposition of the coating increased hardness by 40 %; the Young's modulus, by 18 %; and elastic recovery, by 25 %. Oxidation tests at 1200 °C demonstrated that the specific mass loss of the alloy with Mo30Si60B10 coating was 1.5-fold lower than that of the uncoated alloy. An 18 μm thick oxide layer based on a-SiВO and containing MoO2 particles was formed on the alloy surface. The coating contributes to a ∼14-fold reduction of oxide layer thick. The increase in oxidation resistance of alloy after coating deposition is related to sealing of substrate defects and formation of an a-SiВO layer with elevated silicon content.</div></div>","PeriodicalId":34140,"journal":{"name":"Open Ceramics","volume":"20 ","pages":"Article 100671"},"PeriodicalIF":2.9000,"publicationDate":"2024-09-10","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2666539524001354/pdfft?md5=f4d37c845da45b3223e556cf4839d164&pid=1-s2.0-S2666539524001354-main.pdf","citationCount":"0","resultStr":"{\"title\":\"The oxidation-resistant Mo30Si60B10 coating for protection of the T2 phase-based molybdenum alloy\",\"authors\":\"A.D. Chertova , A. Yu. Potanin , P. Feng , X. Ren , E.A. Levashov , Ph. V. Kiryukhantsev-Korneev\",\"doi\":\"10.1016/j.oceram.2024.100671\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><div>This study focuses on fabrication of a Mo30Si60B10 coating with elevated silicon content, which enhances working properties of Mo-alloy based on the Т2 phase (t-Mo5SiB2). The Mo30Si60B10 coating has a columnar structure. The alloy is characterized by hardness of 17 GPa; Young's modulus of 304 GPa, and elastic recovery of 29 %. Deposition of the coating increased hardness by 40 %; the Young's modulus, by 18 %; and elastic recovery, by 25 %. Oxidation tests at 1200 °C demonstrated that the specific mass loss of the alloy with Mo30Si60B10 coating was 1.5-fold lower than that of the uncoated alloy. An 18 μm thick oxide layer based on a-SiВO and containing MoO2 particles was formed on the alloy surface. The coating contributes to a ∼14-fold reduction of oxide layer thick. The increase in oxidation resistance of alloy after coating deposition is related to sealing of substrate defects and formation of an a-SiВO layer with elevated silicon content.</div></div>\",\"PeriodicalId\":34140,\"journal\":{\"name\":\"Open Ceramics\",\"volume\":\"20 \",\"pages\":\"Article 100671\"},\"PeriodicalIF\":2.9000,\"publicationDate\":\"2024-09-10\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.sciencedirect.com/science/article/pii/S2666539524001354/pdfft?md5=f4d37c845da45b3223e556cf4839d164&pid=1-s2.0-S2666539524001354-main.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Open Ceramics\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S2666539524001354\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, CERAMICS\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Open Ceramics","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2666539524001354","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}

引用次数: 0

摘要

本研究的重点是制作硅含量较高的 Mo30Si60B10 涂层，以提高基于Т2 相的钼合金（t-Mo5SiB2）的工作性能。Mo30Si60B10 涂层具有柱状结构。该合金的硬度为 17 GPa，杨氏模量为 304 GPa，弹性恢复率为 29%。涂层的沉积使硬度提高了 40%，杨氏模量提高了 18%，弹性恢复提高了 25%。1200 °C 下的氧化测试表明，带有 Mo30Si60B10 涂层的合金的比质量损失比没有涂层的合金低 1.5 倍。合金表面形成了 18 μm 厚的氧化层，该氧化层以 a-SiВO 为基础，并含有 MoO2 颗粒。该涂层使氧化层厚度减少了 14 倍。涂层沉积后合金抗氧化性的提高与基底缺陷的密封和硅含量增加的 a-SiВO 层的形成有关。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

The oxidation-resistant Mo30Si60B10 coating for protection of the T2 phase-based molybdenum alloy

查看原文本刊更多论文

The oxidation-resistant Mo30Si60B10 coating for protection of the T2 phase-based molybdenum alloy

This study focuses on fabrication of a Mo₃₀Si₆₀B₁₀ coating with elevated silicon content, which enhances working properties of Mo-alloy based on the Т₂ phase (t-Mo₅SiB₂). The Mo₃₀Si₆₀B₁₀ coating has a columnar structure. The alloy is characterized by hardness of 17 GPa; Young's modulus of 304 GPa, and elastic recovery of 29 %. Deposition of the coating increased hardness by 40 %; the Young's modulus, by 18 %; and elastic recovery, by 25 %. Oxidation tests at 1200 °C demonstrated that the specific mass loss of the alloy with Mo₃₀Si₆₀B₁₀ coating was 1.5-fold lower than that of the uncoated alloy. An 18 μm thick oxide layer based on a-SiВO and containing MoO₂ particles was formed on the alloy surface. The coating contributes to a ∼14-fold reduction of oxide layer thick. The increase in oxidation resistance of alloy after coating deposition is related to sealing of substrate defects and formation of an a-SiВO layer with elevated silicon content.