Imran S. Khan, William E. McMahon, Chun-Sheng Jiang, Patrick Walker, Andriy Zakutayev and Andrew G. Norman*,
{"title":"脉冲激光沉积外延 SrTiO3/Sr3Al2O6 模板作为 GaAs 生长和脱落的水溶性牺牲层","authors":"Imran S. Khan, William E. McMahon, Chun-Sheng Jiang, Patrick Walker, Andriy Zakutayev and Andrew G. Norman*, ","doi":"10.1021/acs.cgd.3c0153110.1021/acs.cgd.3c01531","DOIUrl":null,"url":null,"abstract":"<p >Despite the record-high efficiency of GaAs solar cells, their terrestrial application is limited due to both the particularly high costs related to the required single-crystal substrates and epitaxial growth. A water-soluble lift-off layer could reduce costs by avoiding the need for toxic and dangerous etchants, substrate repolishing, and expensive process steps. Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> (SAO) is a water-soluble cubic oxide, and SrTiO<sub>3</sub> (STO) is a perovskite oxide, where <i>a</i><sub>SAO</sub> ≈ 4 × <i>a</i><sub>STO</sub> ≈ (2√2)<i>a</i><sub>GaAs</sub>. Here, the pulsed laser-deposited epitaxial growth of SrTiO<sub>3</sub>/Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> templates on STO and Ge substrates for epitaxial GaAs growth was investigated, where SAO works as a sacrificial layer and STO protects the hygroscopic SAO during substrate transfer between deposition chambers. We identified that the SAO film quality is strongly dependent on the growth temperature and the O<sub>2</sub> partial pressure, where either a high <i>T</i> or a high <i>P</i>(O<sub>2</sub>) improves the quality. XRD spectra of the films with optimized deposition parameters showed an epitaxial STO/SAO stack aligned to the STO (100) substrate, and TEM analysis revealed that the grown films were epitaxially crystalline throughout the thickness. The STO/SAO growth on Ge substrates at a high <i>T</i> with no intentional O<sub>2</sub> flow resulted in some nonepitaxial grains and surface pits, likely due to partial Ge oxidation. GaAs was grown by metalorganic vapor-phase epitaxy (MOVPE) on STO/SAO/STO templates. Lift-off after dissolving the sacrificial SAO in water resulted in free-standing ⟨001⟩ preferentially oriented polycrystalline GaAs.</p><p >GaAs was epitaxially lifted off from a SrTiO<sub>3</sub> substrate using Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> as a water-soluble sacrificial layer, resulting in ⟨001⟩ preferentially oriented polycrystalline free-standing GaAs films.</p>","PeriodicalId":3,"journal":{"name":"ACS Applied Electronic Materials","volume":null,"pages":null},"PeriodicalIF":4.3000,"publicationDate":"2024-08-28","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://pubs.acs.org/doi/epdf/10.1021/acs.cgd.3c01531","citationCount":"0","resultStr":"{\"title\":\"Pulsed Laser Deposition of Epitaxial SrTiO3/Sr3Al2O6 Templates as a Water-Soluble Sacrificial Layer for GaAs Growth and Lift-Off\",\"authors\":\"Imran S. Khan, William E. McMahon, Chun-Sheng Jiang, Patrick Walker, Andriy Zakutayev and Andrew G. Norman*, \",\"doi\":\"10.1021/acs.cgd.3c0153110.1021/acs.cgd.3c01531\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p >Despite the record-high efficiency of GaAs solar cells, their terrestrial application is limited due to both the particularly high costs related to the required single-crystal substrates and epitaxial growth. A water-soluble lift-off layer could reduce costs by avoiding the need for toxic and dangerous etchants, substrate repolishing, and expensive process steps. Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> (SAO) is a water-soluble cubic oxide, and SrTiO<sub>3</sub> (STO) is a perovskite oxide, where <i>a</i><sub>SAO</sub> ≈ 4 × <i>a</i><sub>STO</sub> ≈ (2√2)<i>a</i><sub>GaAs</sub>. Here, the pulsed laser-deposited epitaxial growth of SrTiO<sub>3</sub>/Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> templates on STO and Ge substrates for epitaxial GaAs growth was investigated, where SAO works as a sacrificial layer and STO protects the hygroscopic SAO during substrate transfer between deposition chambers. We identified that the SAO film quality is strongly dependent on the growth temperature and the O<sub>2</sub> partial pressure, where either a high <i>T</i> or a high <i>P</i>(O<sub>2</sub>) improves the quality. XRD spectra of the films with optimized deposition parameters showed an epitaxial STO/SAO stack aligned to the STO (100) substrate, and TEM analysis revealed that the grown films were epitaxially crystalline throughout the thickness. The STO/SAO growth on Ge substrates at a high <i>T</i> with no intentional O<sub>2</sub> flow resulted in some nonepitaxial grains and surface pits, likely due to partial Ge oxidation. GaAs was grown by metalorganic vapor-phase epitaxy (MOVPE) on STO/SAO/STO templates. Lift-off after dissolving the sacrificial SAO in water resulted in free-standing ⟨001⟩ preferentially oriented polycrystalline GaAs.</p><p >GaAs was epitaxially lifted off from a SrTiO<sub>3</sub> substrate using Sr<sub>3</sub>Al<sub>2</sub>O<sub>6</sub> as a water-soluble sacrificial layer, resulting in ⟨001⟩ preferentially oriented polycrystalline free-standing GaAs films.</p>\",\"PeriodicalId\":3,\"journal\":{\"name\":\"ACS Applied Electronic Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.3000,\"publicationDate\":\"2024-08-28\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://pubs.acs.org/doi/epdf/10.1021/acs.cgd.3c01531\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"ACS Applied Electronic Materials\",\"FirstCategoryId\":\"92\",\"ListUrlMain\":\"https://pubs.acs.org/doi/10.1021/acs.cgd.3c01531\",\"RegionNum\":3,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"ENGINEERING, ELECTRICAL & ELECTRONIC\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"ACS Applied Electronic Materials","FirstCategoryId":"92","ListUrlMain":"https://pubs.acs.org/doi/10.1021/acs.cgd.3c01531","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"ENGINEERING, ELECTRICAL & ELECTRONIC","Score":null,"Total":0}
引用次数: 0
摘要
尽管砷化镓太阳能电池的效率创下了历史新高,但由于所需单晶衬底和外延生长的成本特别高,其在地面上的应用受到了限制。水溶性脱膜层可以避免使用有毒和危险的蚀刻剂、基底重新抛光和昂贵的工艺步骤,从而降低成本。Sr3Al2O6 (SAO) 是一种水溶性立方氧化物,SrTiO3 (STO) 是一种包晶氧化物,其中 aSAO ≈ 4 × aSTO ≈ (2√2)aGaAs。在此,我们研究了 SrTiO3/Sr3Al2O6 模板在 STO 和 Ge 基底上的脉冲激光沉积外延生长,以实现 GaAs 的外延生长,其中 SAO 起着牺牲层的作用,而 STO 则在沉积室之间的基底转移过程中保护吸湿的 SAO。我们发现 SAO 薄膜的质量与生长温度和氧气分压密切相关,高温度或高 P(O2) 都会提高质量。优化沉积参数后薄膜的 XRD 光谱显示,STO/SAO 叠层外延对准了 STO (100) 基质,而 TEM 分析表明,生长的薄膜在整个厚度上都是外延结晶。STO/SAO 在 Ge 衬底上以高 T 生长,没有有意的 O2 流动,结果产生了一些非外延晶粒和表面凹坑,这可能是由于部分 Ge 氧化造成的。砷化镓是在 STO/SAO/STO 模板上通过金属有机气相外延(MOVPE)生长的。使用 Sr3Al2O6 作为水溶性牺牲层,从 SrTiO3 基底上外延生长出了 GaAs,并形成了⟨001⟩优先取向的多晶独立 GaAs 薄膜。
Pulsed Laser Deposition of Epitaxial SrTiO3/Sr3Al2O6 Templates as a Water-Soluble Sacrificial Layer for GaAs Growth and Lift-Off
Despite the record-high efficiency of GaAs solar cells, their terrestrial application is limited due to both the particularly high costs related to the required single-crystal substrates and epitaxial growth. A water-soluble lift-off layer could reduce costs by avoiding the need for toxic and dangerous etchants, substrate repolishing, and expensive process steps. Sr3Al2O6 (SAO) is a water-soluble cubic oxide, and SrTiO3 (STO) is a perovskite oxide, where aSAO ≈ 4 × aSTO ≈ (2√2)aGaAs. Here, the pulsed laser-deposited epitaxial growth of SrTiO3/Sr3Al2O6 templates on STO and Ge substrates for epitaxial GaAs growth was investigated, where SAO works as a sacrificial layer and STO protects the hygroscopic SAO during substrate transfer between deposition chambers. We identified that the SAO film quality is strongly dependent on the growth temperature and the O2 partial pressure, where either a high T or a high P(O2) improves the quality. XRD spectra of the films with optimized deposition parameters showed an epitaxial STO/SAO stack aligned to the STO (100) substrate, and TEM analysis revealed that the grown films were epitaxially crystalline throughout the thickness. The STO/SAO growth on Ge substrates at a high T with no intentional O2 flow resulted in some nonepitaxial grains and surface pits, likely due to partial Ge oxidation. GaAs was grown by metalorganic vapor-phase epitaxy (MOVPE) on STO/SAO/STO templates. Lift-off after dissolving the sacrificial SAO in water resulted in free-standing ⟨001⟩ preferentially oriented polycrystalline GaAs.
GaAs was epitaxially lifted off from a SrTiO3 substrate using Sr3Al2O6 as a water-soluble sacrificial layer, resulting in ⟨001⟩ preferentially oriented polycrystalline free-standing GaAs films.