{"title":"超高温高熵 (Ti0.2Zr0.2Hf0.2Mo0.2W0.2)B2 基陶瓷的加工和表征：W 粒度、石墨和碳化硅添加量的影响","authors":"","doi":"10.1016/j.jallcom.2024.176492","DOIUrl":null,"url":null,"abstract":"<div><p>A highly dense and single phase (Ti<sub>0.2</sub>Zr<sub>0.2</sub>Hf<sub>0.2</sub>Mo<sub>0.2</sub>W<sub>0.2</sub>)B<sub>2</sub> ceramic product is obtained in this work at 1950°C (20 min, 20 MPa) by Spark Plasma Sintering (SPS) from powders prepared by Self-propagating High-temperature Synthesis (SHS). The formation of the (W,Mo)B<sub>2</sub> secondary phase is avoided using fine W precursors and adding 1 wt% graphite to the SHS powders before SPS. Kinetic limitations responsible for hindering the synthesis of the high entropy boride are correspondingly eliminated. The resulting 98.5 % dense sample exhibits a homogeneous microstructure, with Vickers hardness of 26.8 GPa. The introduction of 20 vol% SiC produces an increase of the K<sub>IC</sub> values from 2.32 to 5.11 MPa m<sup>1/2</sup>. Very relevant is that the volatilization of Mo- and W-oxides occurring during sample oxidation at high temperature, which leads to its rapid degradation with the formation of a very porous oxide scale, can be strongly inhibited by the silicate phases generated in the composite ceramic.</p></div>","PeriodicalId":344,"journal":{"name":"Journal of Alloys and Compounds","volume":null,"pages":null},"PeriodicalIF":5.8000,"publicationDate":"2024-09-13","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S0925838824030792/pdfft?md5=9b9c4cb2344527a34857052eed6fb864&pid=1-s2.0-S0925838824030792-main.pdf","citationCount":"0","resultStr":"{\"title\":\"Processing and characterization of Ultra High Temperature High‐Entropy (Ti0.2Zr0.2Hf0.2Mo0.2W0.2)B2-based Ceramics: Effect of W granulometry, graphite, and SiC addition\",\"authors\":\"\",\"doi\":\"10.1016/j.jallcom.2024.176492\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>A highly dense and single phase (Ti<sub>0.2</sub>Zr<sub>0.2</sub>Hf<sub>0.2</sub>Mo<sub>0.2</sub>W<sub>0.2</sub>)B<sub>2</sub> ceramic product is obtained in this work at 1950°C (20 min, 20 MPa) by Spark Plasma Sintering (SPS) from powders prepared by Self-propagating High-temperature Synthesis (SHS). The formation of the (W,Mo)B<sub>2</sub> secondary phase is avoided using fine W precursors and adding 1 wt% graphite to the SHS powders before SPS. Kinetic limitations responsible for hindering the synthesis of the high entropy boride are correspondingly eliminated. The resulting 98.5 % dense sample exhibits a homogeneous microstructure, with Vickers hardness of 26.8 GPa. The introduction of 20 vol% SiC produces an increase of the K<sub>IC</sub> values from 2.32 to 5.11 MPa m<sup>1/2</sup>. Very relevant is that the volatilization of Mo- and W-oxides occurring during sample oxidation at high temperature, which leads to its rapid degradation with the formation of a very porous oxide scale, can be strongly inhibited by the silicate phases generated in the composite ceramic.</p></div>\",\"PeriodicalId\":344,\"journal\":{\"name\":\"Journal of Alloys and Compounds\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":5.8000,\"publicationDate\":\"2024-09-13\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.sciencedirect.com/science/article/pii/S0925838824030792/pdfft?md5=9b9c4cb2344527a34857052eed6fb864&pid=1-s2.0-S0925838824030792-main.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Alloys and Compounds\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0925838824030792\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, PHYSICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Alloys and Compounds","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0925838824030792","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, PHYSICAL","Score":null,"Total":0}
Processing and characterization of Ultra High Temperature High‐Entropy (Ti0.2Zr0.2Hf0.2Mo0.2W0.2)B2-based Ceramics: Effect of W granulometry, graphite, and SiC addition
A highly dense and single phase (Ti0.2Zr0.2Hf0.2Mo0.2W0.2)B2 ceramic product is obtained in this work at 1950°C (20 min, 20 MPa) by Spark Plasma Sintering (SPS) from powders prepared by Self-propagating High-temperature Synthesis (SHS). The formation of the (W,Mo)B2 secondary phase is avoided using fine W precursors and adding 1 wt% graphite to the SHS powders before SPS. Kinetic limitations responsible for hindering the synthesis of the high entropy boride are correspondingly eliminated. The resulting 98.5 % dense sample exhibits a homogeneous microstructure, with Vickers hardness of 26.8 GPa. The introduction of 20 vol% SiC produces an increase of the KIC values from 2.32 to 5.11 MPa m1/2. Very relevant is that the volatilization of Mo- and W-oxides occurring during sample oxidation at high temperature, which leads to its rapid degradation with the formation of a very porous oxide scale, can be strongly inhibited by the silicate phases generated in the composite ceramic.
期刊介绍：
The Journal of Alloys and Compounds is intended to serve as an international medium for the publication of work on solid materials comprising compounds as well as alloys. Its great strength lies in the diversity of discipline which it encompasses, drawing together results from materials science, solid-state chemistry and physics.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号