{"title":"染色、上釉和抛光对氧化锆整体冠存活概率的影响","authors":"Lívia Fiorin, Stephanie Francoi Poole, Paulo Eduardo Barros Souza Oliveira, Adriana Claudia Lapria Faria, Ricardo Faria Ribeiro, Renata Cristina Silveira Rodrigues","doi":"10.1111/jerd.13310","DOIUrl":null,"url":null,"abstract":"<p><strong>Objective: </strong>The purpose of this in vitro study was to evaluate the effect of staining, glazing, and polishing on the survival probability of monolithic crowns manufactured with preshaded stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP).</p><p><strong>Materials and methods: </strong>Monolithic crowns in the shape of an upper canine (1.5 mm of thickness) were manufactured by CAD/CAM, adhesively cemented on metallic foundation, and divided into 6 groups (n = 21): C (control), S (staining), G (glazing), P (polishing), SG (staining and glazing), and SP (staining and polishing). The survival probability was determined by step-stress accelerated life testing with a load applied to the palatine concavity of the crown. First, the specimens were subjected to a single-load to fracture test (SLF) and next to the fatigue test (5 Hz, thermocycling immersed in water varying 5-55°C), including the light (n = 9), moderate (n = 6), and aggressive (n = 3) loading profiles (load ranged between 20% and 60% of SLF). The survival probability was calculated considering the cycles for failure (CFF) and fatigue failure load (FFL) and illustrated using a Kaplan-Meier graph. The comparison among groups was performed using a Log-Rank test (α = 0.05).</p><p><strong>Results: </strong>The mean value of SLF was 586.7 N. There was no difference among groups in survival probability, considering CFF and FFL.</p><p><strong>Conclusion: </strong>Staining, glazing, and polishing can be performed safely without damaging the mechanical behavior of 5Y-TZP monolithic crowns.</p><p><strong>Clinical significance: </strong>Staining is used to characterize and improve the esthetic of zirconia monolithic crowns. It can be used to reproduce the color gradient in the cervical region of the crown and pigmented grooves. This study showed that staining, glazing, and polishing did not affect the survival probability and the use of finishing procedures (glazing or polishing) after staining did not improve the survival probability of zirconia monolithic crowns.</p>","PeriodicalId":15988,"journal":{"name":"Journal of Esthetic and Restorative Dentistry","volume":null,"pages":null},"PeriodicalIF":3.2000,"publicationDate":"2024-09-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Staining, Glazing and Polishing on the Survival Probability of Monolithic Zirconia Crowns.\",\"authors\":\"Lívia Fiorin, Stephanie Francoi Poole, Paulo Eduardo Barros Souza Oliveira, Adriana Claudia Lapria Faria, Ricardo Faria Ribeiro, Renata Cristina Silveira Rodrigues\",\"doi\":\"10.1111/jerd.13310\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Objective: </strong>The purpose of this in vitro study was to evaluate the effect of staining, glazing, and polishing on the survival probability of monolithic crowns manufactured with preshaded stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP).</p><p><strong>Materials and methods: </strong>Monolithic crowns in the shape of an upper canine (1.5 mm of thickness) were manufactured by CAD/CAM, adhesively cemented on metallic foundation, and divided into 6 groups (n = 21): C (control), S (staining), G (glazing), P (polishing), SG (staining and glazing), and SP (staining and polishing). The survival probability was determined by step-stress accelerated life testing with a load applied to the palatine concavity of the crown. First, the specimens were subjected to a single-load to fracture test (SLF) and next to the fatigue test (5 Hz, thermocycling immersed in water varying 5-55°C), including the light (n = 9), moderate (n = 6), and aggressive (n = 3) loading profiles (load ranged between 20% and 60% of SLF). The survival probability was calculated considering the cycles for failure (CFF) and fatigue failure load (FFL) and illustrated using a Kaplan-Meier graph. The comparison among groups was performed using a Log-Rank test (α = 0.05).</p><p><strong>Results: </strong>The mean value of SLF was 586.7 N. There was no difference among groups in survival probability, considering CFF and FFL.</p><p><strong>Conclusion: </strong>Staining, glazing, and polishing can be performed safely without damaging the mechanical behavior of 5Y-TZP monolithic crowns.</p><p><strong>Clinical significance: </strong>Staining is used to characterize and improve the esthetic of zirconia monolithic crowns. It can be used to reproduce the color gradient in the cervical region of the crown and pigmented grooves. This study showed that staining, glazing, and polishing did not affect the survival probability and the use of finishing procedures (glazing or polishing) after staining did not improve the survival probability of zirconia monolithic crowns.</p>\",\"PeriodicalId\":15988,\"journal\":{\"name\":\"Journal of Esthetic and Restorative Dentistry\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":3.2000,\"publicationDate\":\"2024-09-03\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Esthetic and Restorative Dentistry\",\"FirstCategoryId\":\"3\",\"ListUrlMain\":\"https://doi.org/10.1111/jerd.13310\",\"RegionNum\":3,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Esthetic and Restorative Dentistry","FirstCategoryId":"3","ListUrlMain":"https://doi.org/10.1111/jerd.13310","RegionNum":3,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Effect of Staining, Glazing and Polishing on the Survival Probability of Monolithic Zirconia Crowns.
Objective: The purpose of this in vitro study was to evaluate the effect of staining, glazing, and polishing on the survival probability of monolithic crowns manufactured with preshaded stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP).
Materials and methods: Monolithic crowns in the shape of an upper canine (1.5 mm of thickness) were manufactured by CAD/CAM, adhesively cemented on metallic foundation, and divided into 6 groups (n = 21): C (control), S (staining), G (glazing), P (polishing), SG (staining and glazing), and SP (staining and polishing). The survival probability was determined by step-stress accelerated life testing with a load applied to the palatine concavity of the crown. First, the specimens were subjected to a single-load to fracture test (SLF) and next to the fatigue test (5 Hz, thermocycling immersed in water varying 5-55°C), including the light (n = 9), moderate (n = 6), and aggressive (n = 3) loading profiles (load ranged between 20% and 60% of SLF). The survival probability was calculated considering the cycles for failure (CFF) and fatigue failure load (FFL) and illustrated using a Kaplan-Meier graph. The comparison among groups was performed using a Log-Rank test (α = 0.05).
Results: The mean value of SLF was 586.7 N. There was no difference among groups in survival probability, considering CFF and FFL.
Conclusion: Staining, glazing, and polishing can be performed safely without damaging the mechanical behavior of 5Y-TZP monolithic crowns.
Clinical significance: Staining is used to characterize and improve the esthetic of zirconia monolithic crowns. It can be used to reproduce the color gradient in the cervical region of the crown and pigmented grooves. This study showed that staining, glazing, and polishing did not affect the survival probability and the use of finishing procedures (glazing or polishing) after staining did not improve the survival probability of zirconia monolithic crowns.
期刊介绍：
The Journal of Esthetic and Restorative Dentistry (JERD) is the longest standing peer-reviewed journal devoted solely to advancing the knowledge and practice of esthetic dentistry. Its goal is to provide the very latest evidence-based information in the realm of contemporary interdisciplinary esthetic dentistry through high quality clinical papers, sound research reports and educational features.
The range of topics covered in the journal includes:
- Interdisciplinary esthetic concepts
- Implants
- Conservative adhesive restorations
- Tooth Whitening
- Prosthodontic materials and techniques
- Dental materials
- Orthodontic, periodontal and endodontic esthetics
- Esthetics related research
- Innovations in esthetics
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号