{"title":"将近红到蓝的上转换发光应用于通过氧化锆盘聚合树脂胶结物。","authors":"","doi":"10.1016/j.dental.2024.06.005","DOIUrl":null,"url":null,"abstract":"<div><h3>Objectives</h3><p>To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs.</p></div><div><h3>Methods</h3><p>Lava zirconia discs of different thicknesses (0.5–2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF<sub>4</sub>:Yb<sup>3+</sup>/Tm<sup>3+</sup> upconversion phosphor (UP) powder was milled into 0.5-μm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type.</p></div><div><h3>Results</h3><p>The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm.</p></div><div><h3>Significance</h3><p>NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.</p></div>","PeriodicalId":298,"journal":{"name":"Dental Materials","volume":null,"pages":null},"PeriodicalIF":4.6000,"publicationDate":"2024-06-08","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Application of near-infrared-to-blue upconversion luminescence for the polymerization of resin cements through zirconia discs\",\"authors\":\"\",\"doi\":\"10.1016/j.dental.2024.06.005\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><h3>Objectives</h3><p>To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs.</p></div><div><h3>Methods</h3><p>Lava zirconia discs of different thicknesses (0.5–2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF<sub>4</sub>:Yb<sup>3+</sup>/Tm<sup>3+</sup> upconversion phosphor (UP) powder was milled into 0.5-μm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type.</p></div><div><h3>Results</h3><p>The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm.</p></div><div><h3>Significance</h3><p>NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.</p></div>\",\"PeriodicalId\":298,\"journal\":{\"name\":\"Dental Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.6000,\"publicationDate\":\"2024-06-08\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Dental Materials\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0109564124001374\",\"RegionNum\":1,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Dental Materials","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0109564124001374","RegionNum":1,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Application of near-infrared-to-blue upconversion luminescence for the polymerization of resin cements through zirconia discs
Objectives
To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs.
Methods
Lava zirconia discs of different thicknesses (0.5–2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF4:Yb3+/Tm3+ upconversion phosphor (UP) powder was milled into 0.5-μm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type.
Results
The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm.
Significance
NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.
期刊介绍:
Dental Materials publishes original research, review articles, and short communications.
Academy of Dental Materials members click here to register for free access to Dental Materials online.
The principal aim of Dental Materials is to promote rapid communication of scientific information between academia, industry, and the dental practitioner. Original Manuscripts on clinical and laboratory research of basic and applied character which focus on the properties or performance of dental materials or the reaction of host tissues to materials are given priority publication. Other acceptable topics include application technology in clinical dentistry and dental laboratory technology.
Comprehensive reviews and editorial commentaries on pertinent subjects will be considered.