Corrosion resistance and conductivity of CrN, CrAlN, and CrTiN coatings applied to bipolar plates for proton exchange membrane fuel cells

In order to improve the corrosion resistance and conductivity of 316L stainless steel bipolar plates used for proton exchange membrane fuel cells, three Cr-containing nitride coatings were deposited on 316L stainless steel by multiarc ion plating. First, the microstructure, composition, and contact angle of the three coatings were systematically investigated. Then, electrochemical impedance spectroscopy, potentiodynamic polarization, potentiostatic polarization (PSP), and interfacial contact resistance (ICR) of the three coatings were also fully examined. The results revealed that CrN coating has the highest contact angle of 98.26°, indicating its superior hydrophobicity. Additionally, CrN coating performed the best corrosion resistance with the highest corrosion potential of 0.31 V, the lowest corrosion current density of 2.28 × 10−7 A cm−2, and the largest resistance. Furthermore, CrN coating showed the lowest current density during PSP tests and the smallest ICR value after corrosion. The superior corrosion resistance of CrN coating is mainly attributed to its decreased pore density caused by vacancylike defects and its uniform structure. This article provided evidence for the potential application of CrN coating to bipolar plates.