{"title":"Ti-6Al-4V 合金与 Inconel 625 超级合金的异种瞬态液相键合：键合温度对微观结构演变和机械性能的影响","authors":"Behnam Zorriatolhosseini, Seyyed Ehsan Mirsalehi, Faezeh Shamsi","doi":"10.1007/s40194-024-01777-7","DOIUrl":null,"url":null,"abstract":"<div><p>The present study investigated the effect of bonding temperature on the dissimilar transient liquid phase (TLP)–bonded IN-625/Ti-6Al-4V dissimilar joints using a thin foil of pure copper as the interlayer. The samples were bonded in a vacuum chamber at 900, 930, and 960 °C for 60 min. The results indicated the occurrence of different intermetallic compounds such as Ti<sub>2</sub>Cu, TiCu<sub>2</sub>, TiCu, NiTi, and Ni<sub>3</sub>Ti at different bonding temperatures, and it was concluded that in all the samples, isothermal solidification was accomplished. Maximum shear strength of 278 MPa was achieved at 930 °C. At lower bonding temperatures, the presence of porosities and cracks decreases the shear strength. At higher temperatures, a high-volume percentage of intermetallic compounds embrittled the specimen and reduced its shear strength. The results of scanning electron microscopy of the fracture surfaces revealed the formation of extensive cleavage fracture and river-like patterns in all samples, indicating a brittle failure mode.</p></div>","PeriodicalId":809,"journal":{"name":"Welding in the World","volume":null,"pages":null},"PeriodicalIF":2.4000,"publicationDate":"2024-04-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Dissimilar transient liquid phase bonding of Ti-6Al-4V alloy to Inconel 625 superalloy: effect of bonding temperature on microstructural evolutions and mechanical properties\",\"authors\":\"Behnam Zorriatolhosseini, Seyyed Ehsan Mirsalehi, Faezeh Shamsi\",\"doi\":\"10.1007/s40194-024-01777-7\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>The present study investigated the effect of bonding temperature on the dissimilar transient liquid phase (TLP)–bonded IN-625/Ti-6Al-4V dissimilar joints using a thin foil of pure copper as the interlayer. The samples were bonded in a vacuum chamber at 900, 930, and 960 °C for 60 min. The results indicated the occurrence of different intermetallic compounds such as Ti<sub>2</sub>Cu, TiCu<sub>2</sub>, TiCu, NiTi, and Ni<sub>3</sub>Ti at different bonding temperatures, and it was concluded that in all the samples, isothermal solidification was accomplished. Maximum shear strength of 278 MPa was achieved at 930 °C. At lower bonding temperatures, the presence of porosities and cracks decreases the shear strength. At higher temperatures, a high-volume percentage of intermetallic compounds embrittled the specimen and reduced its shear strength. The results of scanning electron microscopy of the fracture surfaces revealed the formation of extensive cleavage fracture and river-like patterns in all samples, indicating a brittle failure mode.</p></div>\",\"PeriodicalId\":809,\"journal\":{\"name\":\"Welding in the World\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":2.4000,\"publicationDate\":\"2024-04-30\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Welding in the World\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://link.springer.com/article/10.1007/s40194-024-01777-7\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"METALLURGY & METALLURGICAL ENGINEERING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Welding in the World","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s40194-024-01777-7","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
Dissimilar transient liquid phase bonding of Ti-6Al-4V alloy to Inconel 625 superalloy: effect of bonding temperature on microstructural evolutions and mechanical properties
The present study investigated the effect of bonding temperature on the dissimilar transient liquid phase (TLP)–bonded IN-625/Ti-6Al-4V dissimilar joints using a thin foil of pure copper as the interlayer. The samples were bonded in a vacuum chamber at 900, 930, and 960 °C for 60 min. The results indicated the occurrence of different intermetallic compounds such as Ti2Cu, TiCu2, TiCu, NiTi, and Ni3Ti at different bonding temperatures, and it was concluded that in all the samples, isothermal solidification was accomplished. Maximum shear strength of 278 MPa was achieved at 930 °C. At lower bonding temperatures, the presence of porosities and cracks decreases the shear strength. At higher temperatures, a high-volume percentage of intermetallic compounds embrittled the specimen and reduced its shear strength. The results of scanning electron microscopy of the fracture surfaces revealed the formation of extensive cleavage fracture and river-like patterns in all samples, indicating a brittle failure mode.
期刊介绍：
The journal Welding in the World publishes authoritative papers on every aspect of materials joining, including welding, brazing, soldering, cutting, thermal spraying and allied joining and fabrication techniques.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号