{"title":"合成具有可调布氏酸度和勒维斯酸度的含铝锡β,用于将葡萄糖转化为 5-羟甲基糠醛","authors":"Yaxin Nie , Yangyang Ma , Jie Hu , Xiaomei Yang , Lipeng Zhou , Yunlai Su","doi":"10.1016/j.micromeso.2024.113157","DOIUrl":null,"url":null,"abstract":"<div><p>Sn–Al-Beta zeolites with less silanol defects were synthesized in fluoride media. The effects of the amount of organic template (tetraethylammonium hydroxide, TEAOH), mineralizer (NH<sub>4</sub>F), Al and Sn on the synthesis, acidity and catalytic performance were systematically studied. The synthesized Sn–Al-Beta zeolites were characterized by XRD, SEM, <sup>27</sup>Al MAS NMR, UV–vis DRS and FT-IR spectroscopy of hydroxy region and pyridine adsorption. The optimum values of <em>n</em><sub>TEAOH</sub>/<em>n</em><sub>Si</sub> and <em>n</em><sub>F-</sub>/<em>n</em><sub>Si</sub> were same (0.3) for synthesizing Sn–Al-Beta with high crystallinity at 140 °C for 7 d. Moreover, decreasing <em>n</em><sub>F-</sub>/<em>n</em><sub>Si</sub> facilitated the incorporation of Al into the framework. The crystallization rate of Sn–Al-Beta is similar with that of Sn-Beta. Sn was promoted to enter the framework with the increase of Al content, while elevating Sn content has no effect on the incorporation of Al into the framework. The catalytic performance of Sn–Al-Beta was investigated for conversion of glucose to 5-hydroxymethylfurfural in water-containing solvent. Sn–Al-Beta synthesized in fluoride media is more stable than the post-synthesized sample.</p></div>","PeriodicalId":392,"journal":{"name":"Microporous and Mesoporous Materials","volume":null,"pages":null},"PeriodicalIF":4.8000,"publicationDate":"2024-04-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Synthesis of Al-containing Sn-beta with tunable brønsted and lewis acidity for conversion of glucose to 5-hydroxymethylfurfural\",\"authors\":\"Yaxin Nie , Yangyang Ma , Jie Hu , Xiaomei Yang , Lipeng Zhou , Yunlai Su\",\"doi\":\"10.1016/j.micromeso.2024.113157\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>Sn–Al-Beta zeolites with less silanol defects were synthesized in fluoride media. The effects of the amount of organic template (tetraethylammonium hydroxide, TEAOH), mineralizer (NH<sub>4</sub>F), Al and Sn on the synthesis, acidity and catalytic performance were systematically studied. The synthesized Sn–Al-Beta zeolites were characterized by XRD, SEM, <sup>27</sup>Al MAS NMR, UV–vis DRS and FT-IR spectroscopy of hydroxy region and pyridine adsorption. The optimum values of <em>n</em><sub>TEAOH</sub>/<em>n</em><sub>Si</sub> and <em>n</em><sub>F-</sub>/<em>n</em><sub>Si</sub> were same (0.3) for synthesizing Sn–Al-Beta with high crystallinity at 140 °C for 7 d. Moreover, decreasing <em>n</em><sub>F-</sub>/<em>n</em><sub>Si</sub> facilitated the incorporation of Al into the framework. The crystallization rate of Sn–Al-Beta is similar with that of Sn-Beta. Sn was promoted to enter the framework with the increase of Al content, while elevating Sn content has no effect on the incorporation of Al into the framework. The catalytic performance of Sn–Al-Beta was investigated for conversion of glucose to 5-hydroxymethylfurfural in water-containing solvent. Sn–Al-Beta synthesized in fluoride media is more stable than the post-synthesized sample.</p></div>\",\"PeriodicalId\":392,\"journal\":{\"name\":\"Microporous and Mesoporous Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.8000,\"publicationDate\":\"2024-04-26\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Microporous and Mesoporous Materials\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S1387181124001793\",\"RegionNum\":3,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"CHEMISTRY, APPLIED\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Microporous and Mesoporous Materials","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1387181124001793","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"CHEMISTRY, APPLIED","Score":null,"Total":0}
引用次数: 0
摘要
在氟化介质中合成了硅醇缺陷较少的 Sn-Al-Beta 沸石。系统研究了有机模板(四乙基氢氧化铵,TEAOH)、矿化剂(NH4F)、Al 和 Sn 的用量对合成、酸度和催化性能的影响。通过 XRD、SEM、27Al MAS NMR、UV-vis DRS 和 FT-IR 光谱分析羟基区和吡啶的吸附情况,对合成的 Sn-Al-Beta 沸石进行了表征。nTEAOH/nSi 和 nF-/nSi 的最佳值(0.3)相同,可在 140 °C 下 7 d 合成高结晶度的 Sn-Al-Beta。Sn-Al-Beta 的结晶速率与 Sn-Beta 相似。随着 Al 含量的增加,Sn 进入框架的速度加快,而 Sn 含量的增加对 Al 进入框架没有影响。研究了 Sn-Al-Beta 在含水溶剂中将葡萄糖转化为 5-羟甲基糠醛的催化性能。在氟介质中合成的 Sn-Al-Beta 比合成后的样品更稳定。
Synthesis of Al-containing Sn-beta with tunable brønsted and lewis acidity for conversion of glucose to 5-hydroxymethylfurfural
Sn–Al-Beta zeolites with less silanol defects were synthesized in fluoride media. The effects of the amount of organic template (tetraethylammonium hydroxide, TEAOH), mineralizer (NH4F), Al and Sn on the synthesis, acidity and catalytic performance were systematically studied. The synthesized Sn–Al-Beta zeolites were characterized by XRD, SEM, 27Al MAS NMR, UV–vis DRS and FT-IR spectroscopy of hydroxy region and pyridine adsorption. The optimum values of nTEAOH/nSi and nF-/nSi were same (0.3) for synthesizing Sn–Al-Beta with high crystallinity at 140 °C for 7 d. Moreover, decreasing nF-/nSi facilitated the incorporation of Al into the framework. The crystallization rate of Sn–Al-Beta is similar with that of Sn-Beta. Sn was promoted to enter the framework with the increase of Al content, while elevating Sn content has no effect on the incorporation of Al into the framework. The catalytic performance of Sn–Al-Beta was investigated for conversion of glucose to 5-hydroxymethylfurfural in water-containing solvent. Sn–Al-Beta synthesized in fluoride media is more stable than the post-synthesized sample.
期刊介绍:
Microporous and Mesoporous Materials covers novel and significant aspects of porous solids classified as either microporous (pore size up to 2 nm) or mesoporous (pore size 2 to 50 nm). The porosity should have a specific impact on the material properties or application. Typical examples are zeolites and zeolite-like materials, pillared materials, clathrasils and clathrates, carbon molecular sieves, ordered mesoporous materials, organic/inorganic porous hybrid materials, or porous metal oxides. Both natural and synthetic porous materials are within the scope of the journal.
Topics which are particularly of interest include:
All aspects of natural microporous and mesoporous solids
The synthesis of crystalline or amorphous porous materials
The physico-chemical characterization of microporous and mesoporous solids, especially spectroscopic and microscopic
The modification of microporous and mesoporous solids, for example by ion exchange or solid-state reactions
All topics related to diffusion of mobile species in the pores of microporous and mesoporous materials
Adsorption (and other separation techniques) using microporous or mesoporous adsorbents
Catalysis by microporous and mesoporous materials
Host/guest interactions
Theoretical chemistry and modelling of host/guest interactions
All topics related to the application of microporous and mesoporous materials in industrial catalysis, separation technology, environmental protection, electrochemistry, membranes, sensors, optical devices, etc.