Suppressed Phase Segregation with Small A-Site and Large X-Site Incorporation for Photostable Wide-Bandgap Perovskite Solar Cells.

Wide-bandgap (WBG) perovskite solar cells (PSCs) have been widely used as the top cell of tandem solar cells. However, photoinduced phase segregation and high open-circuit voltage loss pose significant obstacles to the development of WBG PSCs. Here, a two-step small-size A-site and large-size X-site incorporation strategy is reported to modulate the lattice distortion and improve the film quality of WBG formamidinium-methylammonium (FAMA) perovskite films for photostable PSCs based on two-step deposition method. First, CsI with content of 0-20% is introduced to tune the lattice distortion and film quality of FAMA perovskite with a bandgap of 1.70 eV. Then, 4% RbI is incorporated to further modulate the perovskite growth and lattice distortion, leading to the suppression of photoinduced phase segregation in the resultant RbCsFAMA quadruple cation perovskites. As a result, the 20%CsI/4%RbI-doped device obtains a promising efficiency of 20.6%, and the corresponding perovskite film shows good photothermal stability. Even without encapsulation, the device can maintain 92% of its initial efficiency after 1000 h of continuous operation under 1 sun equivalent white light-emitting diode illumination.