Elemental composition, corrosion resistance and mechanical properties of computer-aided design and computer-aided manufacturing fixed retainers versus conventional fixed retainers

Purpose: To investigate the elemental composition, corrosion resistance, and mechanical properties of computer-aided design and computer-aided manufacturing (CAD-CAM) retainers versus conventional fixed retainers (FRs).

Methods: Eight different retainer wires were investigated. Energy dispersive X-ray spectroscopy was used to determine the elemental composition. Leakage was analysed according to ISO 10271:2020 guidelines. Hardness was tested using the Vickers method with a load of 0.3 kg. The tensile force and tensile strength were evaluated. Multiple comparisons among wires of hardness, tensile force, and strength were conducted using the Welch t-test, with Bonferroni correction.

Results: Nickel was present in all wires. The CAD-CAM-FR wire, which contained more nickel than the other wires, had no measurable leakage. The gold-plated wires had the highest total leakage, but did not exceed the ISO standard limit. The hardness of the stainless-steel twisted wires was the highest and that of the CAD-CAM-FR wire was the lowest. The tensile strength of the CAD-CAM-FR wire was significantly lower than that of the other wires and similar to the other twisted-wire retainers.

Conclusion: The CAD-CAM-FR wire is likely to have high corrosion resistance and flexibility due to its low hardness.