{"title":"注地层水用钢管道损坏原因调查","authors":"R. Jachym, P. Gotkowski, J. Gazdowicz","doi":"10.17729/ebis.2020.3/3","DOIUrl":null,"url":null,"abstract":"The article presents results of the research on the causes of failure of the DN 80 steel pipeline used for injection of formation waters. Based on the research results, it was found that the cause of perforation and subsequent material losses in the DN 80 pipeline wall made of L360NB steel was under deposit corrosion.","PeriodicalId":184101,"journal":{"name":"Biuletyn Instytutu Spawalnictwa","volume":"7 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2020-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Investigation of Reasons for Damage to a Steel Pipeline Used For the Injection of Formation Waters\",\"authors\":\"R. Jachym, P. Gotkowski, J. Gazdowicz\",\"doi\":\"10.17729/ebis.2020.3/3\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The article presents results of the research on the causes of failure of the DN 80 steel pipeline used for injection of formation waters. Based on the research results, it was found that the cause of perforation and subsequent material losses in the DN 80 pipeline wall made of L360NB steel was under deposit corrosion.\",\"PeriodicalId\":184101,\"journal\":{\"name\":\"Biuletyn Instytutu Spawalnictwa\",\"volume\":\"7 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2020-06-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Biuletyn Instytutu Spawalnictwa\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.17729/ebis.2020.3/3\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Biuletyn Instytutu Spawalnictwa","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.17729/ebis.2020.3/3","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Investigation of Reasons for Damage to a Steel Pipeline Used For the Injection of Formation Waters
The article presents results of the research on the causes of failure of the DN 80 steel pipeline used for injection of formation waters. Based on the research results, it was found that the cause of perforation and subsequent material losses in the DN 80 pipeline wall made of L360NB steel was under deposit corrosion.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号