Green synthesis of copper oxide nanoparticles from Murraya koenigii and its corrosion resistivity on Ti-6Al-4V dental alloy

The present work describes green-mediated copper oxide nanoparticles as a potential corrosion inhibitor for the dental alloy Ti-6Al-4V. The salt of copper was reduced to metal nanoparticles using Murraya koenigii leaves, which helps with the agglomeration and nanocluster formation through a reduction mechanism. The current synthesis is a single-step process and is cost-effective. The synthesized nanoparticle was characterized using UV, FTIR, XRD, Zeta potential and Particle size analyzer, SEM, and EDX. The particles were then electrodeposited on Ti-6Al-4V alloy, and the corrosion resistivity in the dental medium was analyzed using Electrochemical parameters such as Corrosion current, Corrosion potential, and anodic and cathodic intercepts through the Tafel and Nyquist plots. The synthesized nanoparticles showed characteristic absorbance at 359 nm. FTIR peaks confirm the phytochemical constituents present in the Murraya koenigii that accounts for the formation of nanoparticles. The XRD predicts the crystalline nature, which is further studied using SEM and EDX. The Zeta potential and Particle size analyzer confirms the negative-negative interactive nature of the synthesized CuO NPs. The NPs showed explicit corrosion inhibition properties with an overall inhibition efficiency of 58.15% and 25.6%, respectively. The study confirms the advantage of using Copper Oxide nanoparticles as a potential coating agent in dental implant alloys in increasing its corrosion efficiency.