Use of Silver Nanoparticles as Tougheners of Alumina Ceramics

Abstract

In this work, alumina/silver composites were produced through powder techniques, which involve the combination of high energy mechanical milling combined with sintering in the presence of a liquid phase and with the idea of having ceramics with good toughness values. From mechanical characterizations, it was found that increases of the silver content in the alumina origins decrease the elastic’s modulus and flexural strength of the final composite. The fracture toughness of alumina increases from 4.2 MPam −0.5 for monolithic alumina to 10 MPam −0.5 for alumina with 2 wt% silver additions. It was determined that the reinforcement mechanism of these materials is due to the deflection of cracks owing to metallic bridges formed by the silver used as toughener material.