Chao Zhang, Ruidong Wang, Rong Hu, Zhiyu Chen, Yuwen Zhang, Xionggang Lu
{"title":"Plasma transferred arc cladding of Ni-Cr-B-Si coating on copper substrate","authors":"Chao Zhang, Ruidong Wang, Rong Hu, Zhiyu Chen, Yuwen Zhang, Xionggang Lu","doi":"10.1016/j.mlblux.2022.100137","DOIUrl":null,"url":null,"abstract":"<div><p>Aiming to improve the surface properties of copper, a Ni-Cr-B-Si coating was fabricated by plasma transferred arc (PTA) cladding. The coating formed a good metallurgical bonding with the copper substrate, and the dilution rate was about 15.9%. The coating mainly contained γ-(Cu, Fe, Ni), Cr<sub>23</sub>C<sub>6</sub>, CrB and Ni<sub>3</sub>Si phases, which played a role of solid solution strengthening and dispersion strengthening. The hardness of the coating was significantly improved compared to the copper substrate, which was approximately 7.8 times that of the substrate. The wear resistance of the coating was 5.0 times higher than that of the copper substrate, and the wear mechanism was abrasive wear.</p></div>","PeriodicalId":18245,"journal":{"name":"Materials Letters: X","volume":"14 ","pages":"Article 100137"},"PeriodicalIF":2.2000,"publicationDate":"2022-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2590150822000175/pdfft?md5=3ca52287202ff392d256df8ffe229fb0&pid=1-s2.0-S2590150822000175-main.pdf","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Letters: X","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2590150822000175","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 2
Abstract
Aiming to improve the surface properties of copper, a Ni-Cr-B-Si coating was fabricated by plasma transferred arc (PTA) cladding. The coating formed a good metallurgical bonding with the copper substrate, and the dilution rate was about 15.9%. The coating mainly contained γ-(Cu, Fe, Ni), Cr23C6, CrB and Ni3Si phases, which played a role of solid solution strengthening and dispersion strengthening. The hardness of the coating was significantly improved compared to the copper substrate, which was approximately 7.8 times that of the substrate. The wear resistance of the coating was 5.0 times higher than that of the copper substrate, and the wear mechanism was abrasive wear.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号