Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation

Abstract

Achieving high mechanical strength and ductility in age-hardenable Al7000 series (Al–Zn–Mg) alloys fabricated by selective laser melting (SLM) remains challenging. Here, we show that crack-free AlZnMgCuScZr alloys with an unprecedented strength–ductility synergy can be fabricated via SLM and heat treatment. The as-built samples had an architectured microstructure consisting of a multimodal grain structure and a hierarchical phase morphology. It consisted of primary Al₃(Sc_x,Zr_1−x) particles which act as inoculants for ultrafine grains, preventing crack formation. The metastable Mg-, Zn-, and Cu-rich icosahedral quasicrystals (I-phase) ubiquitously dispersed inside the grains and aligned as a filigree skeleton along the grain boundaries. The heat treated SLM-produced AlZnMgCuScZr alloy exhibited tunable mechanical behaviors through trade-off among the hierarchical features, including the dual-nanoprecipitation, viz, η′ phase, and secondary (Al,Zn)₃(Sc₉Zr), and grain coarsening. Less coarsening of grains and (Al,Zn)₃(Sc₉Zr) particles, due to a reduced solution treatment temperature and time, could overwhelm the more complete dissolution of I-phase (triggering more η′ phase), resulting in higher yield strength. Optimal combination of the hierarchical features yields the highest yield strength (∼647 MPa) among all reported SLM-produced Al alloys to date with appreciable ductility (∼11.6%). The successful fabrication of high-strength Al7000 series alloys with an adjustable hierarchical microstructure paves the way for designing and fine-tuning SLM-produced aluminum engineering components exposed to high mechanical loads.