Experimental Study on Mechanical Properties of Thermally Conductive High-Strength Concrete.

Abstract

Ultra-high-performance concrete (UHPC) is considered one of the future building materials due to its excellent performance. UHPC with good thermal conductivity has potential high-value applications in large-scale bridges and nuclear facilities. As a by-product of the coal gasification process, coal gasification slag (CGS) can replace sand in traditional UHPC. In this paper, based on the preparation of UHPC by CGS, silicon carbide (SiC) was added to improve the thermal conductivity of specimens. The application of CGS and SiC as alternatives to quartz sand with varying mix ratios in UHPC was studied. The impact of the substitution ratios of CGS and SiC on fluidity, mechanical properties, and thermal performance was analyzed. The compressive strength and splitting tensile strength of five different kinds of specimens were tested at 7 d, 14 d, and 28 d. The compressive strength and mass loss rate of specimens with five different ratios were also determined under five different temperature conditions (110 °C, 200 °C, 300 °C, 400 °C, and 500 °C). The results show that the maximum compressive strength of 28 d can reach 159.5 MPa and the splitting strength is 15.30 MPa. The addition of SiC can improve the thermal conductivity and thermal stability of concrete. The compressive strength of all specimens is improved after high-temperature treatment. When substitution rate of SiC reaches 100%, the compressive strength of the specimens is up to 182.2 MPa. With the increase in temperature, the concrete burst phenomenon occurs above 300 °C. It is observed that the high-temperature burst resistance of the specimens with low strength is better than that of the specimens with high strength. Two specimens were scanned with Industrial Computerized Tomography (ICT) and the microstructures of the specimens were compared. It was found that the samples with higher SiC substitution rates had more minor total pore defects and larger pores.