Effects of electron beam and atomic oxygen irradiation on hypervelocity - Impact tested / polyimide coated carbon fiber-reinforced plates

Abstract

In a low-Earth orbit, space debris orbit at approximately the first cosmic velocity. When space debris strike a spacecraft, ejecta (fragments) from the spacecraft are widely scattered. The reduction in the number of ejecta (fragments caused by impact) must also be considered when selecting spacecraft materials. The authors’ group has previously examined the size of ejecta (fragments) and reduction in the number of ejecta. In general, the mechanical properties of polymer materials and CFRP plates may be damaged by space environments, such as radiation (gamma rays and electron beams (EBs)), atomic oxygen (AO), ultraviolet rays, temperature, and thermal cycling. The authors suggested an anti-AO coating/polyimide CFRP as a material resistant to space environments. The effects of EB and AO irradiation on the fracture behavior and ejecta of anti-AO coating/polyimide CFRP were examined for hypervelocity impacts. The results of static three-point flexural tests were compared with the fracture behavior and ejecta. A two-stage light-gas gun was used for the impact tests. Spherical projectiles formed of aluminum alloy 2017-T4 with a diameter of 1.6 mm were used. Photographs of the ejecta scattered in front of each polyimide CFRP plate were captured from the side using a high-speed video camera. The number and weight of the ejecta on the front side and perforation holes were examined.