Microstructure and mechanical properties of wire and arc additive manufactured 2319 aluminum alloy treated by laser shock peening

Abstract

The components manufactured by Wire and Arc Additive Manufacturing (WAAM) have some problems to be solved urgently, such as uneven microstructure, numerous pore defects, and residual tensile stress. Laser Shock Peening (LSP) is an innovative and advanced surface modification technology that improves mechanical characteristics by inducing significant plastic deformation and high compressive residual stress on metal surfaces. Therefore, combining LSP with WAAM is expected to solve its existing problems. In this work, LSP with different energy parameters was used to post-process the WAAM 2319 aluminum alloy. The results indicated that LSP could improve the microstructure, eliminate near-surface pores, harden the surface layer, and induce a residual compressive stress layer, and the effect was more effective with the increase of laser energy applied. The yield strength of the peened specimens significantly increased by 60.73 %, and the ultimate tensile strength also increased by 16.03 %. The hole fatigue life of the peened specimens was significantly improved, increasing by 179.8 % and 261.7 %, respectively, applying laser energies of 5 J and 10 J. Therefore, the engineering industry may benefit from a combination of LSP and WAAM technology.