Effect of Laser Beam Overlap Rate on Mechanical Properties of Aluminum Alloy Arc Welding with Laser Peening

Abstract

This study aims to investigate the effect of the laser beam overlap rate on the mechanical properties of Al3003 aluminum alloy arc weldment with laser peening. To determine the optimal laser beam overlap rate for laser peening of the weldment, peening experiments were conducted on bead-welded and butt-welded specimens with varying overlap rates, and the effect of the beam overlap rate was analyzed. As the overlap rate increased, the residual stress changed from tensile to compressive, with the highest level of compressive residual stress at the overlap rate of 75%. Laser peening was performed on the aluminum weldment of the prototype, applying the optimal peening conditions identified earlier. As a result of comparing the residual stress, hardness, and tensile strength of the weld before and after laser peening, it was found that the tensile residual stress in the weldment was improved to a compressive residual stress of about −50 MPa or more. The hardness and tensile strength of the weld increased after peening, and the mechanical properties were also improved.