Evaluation of Shear-Punched Surface Layer Damage in Ultrahigh-Strength TRIP-Aided Steels with Bainitic Ferrite and/or Martensite Matrix Structure

Abstract

The damage to the shear-punched surface layers such as strain-hardening, strain-induced martensite transformation, and micro-void initiation behaviors was evaluated in the third-generation low-carbon advanced ultrahigh-strength TRIP-aided bainitic ferrite (TBF), bainitic ferrite–martensite (TBM), and martensite (TM) steels. In addition, the surface layer damage was related to (1) the mean normal stress generated during shear-punching and (2) microstructural properties such as the matrix structure, retained austenite characteristics, and second-phase properties. The shear-punched surface layer damage was produced under the mean normal stress between zero and negative in all the steels. The TBM and TM steels achieved relatively small surface layer damage. The small surface layer damage resulted in excellent cold stretch-flangeability, with a high crack-propagation/void-connection resistance on hole expansion.