Research on influence factors of small punch test to evaluate the mechanical properties of gradient nanostructured material

Abstract

The influence factors of small punch test (SPT) were investigated to evaluate the mechanical properties of gradient nanostructured (GNS) materials. The gradient nanostructure was prepared on the top layer of S30408 austenitic stainless steel by ultrasonic impact treatment (UIT). The mechanical properties of the GNS material were obtained using SPT and correlated with those obtained by standard tensile tests. The results indicate that, when the specimen thickness is 0.5 mm, the sphere diameter is 2.4 mm, the punch velocity is 0.5 mm min⁻¹, and the gradient nano-grained layer is placed face-on in the mold, the GNS material exhibits better plastic deformability. The SPT specimen achieves better bearing capacity, and the mechanical properties of the GNS material obtained by SPT are more accurate. The yield strength and tensile strength of the GNS material were also evaluated by analytical and empirical methods in SPT. The error is approximately 10% compared with the standard tensile test results, which is within the allowable range.