Xiaobiao An , Xianzhou Lyu , Jiecheng Sun , Zhukai Liu , Weiming Wang
{"title":"Mechanical behaviour and macro-micro failure mechanisms of frozen weakly cemented sandstone under different stress paths","authors":"Xiaobiao An , Xianzhou Lyu , Jiecheng Sun , Zhukai Liu , Weiming Wang","doi":"10.1016/j.conbuildmat.2024.138264","DOIUrl":null,"url":null,"abstract":"<div><p>Significant unloading failure zones in artificial freezing shaft sinking projects in western China are primarily caused by stress release. To investigate the deformation and failure mechanisms of frozen weakly cemented sandstone (FWCS), three groups of triaxial unloading tests were conducted under different initial principal stresses (σ₃ = 3, 6, and 10 MPa) with an unloading rate of 0.05 MPa/s. Scanning electron microscopy (SEM) was employed to examine the micro-fracture characteristics of the failure surfaces. The results revealed that, compared to traditional triaxial and room-temperature triaxial compression tests, the strength and plastic deformation characteristics of FWCS are significantly weakened under unloading conditions. However, lateral deformation, particularly volumetric strain, increased markedly, exhibiting pronounced dilatancy characteristics, especially along stress path III (i.e., post-peak axial stress loading with confining pressure unloading). Unloading leads to a reduction in cohesion and an increase in the internal friction angle of FWCS, with the most significant changes observed along stress path IV (i.e., pre-peak constant axial displacement loading with confining pressure unloading). Macroscopic and microscopic analyses indicate that the failure mechanism of FWCS under complex unloading stress paths is driven by the rapid accumulation of energy caused by unloading, which results in the development and propagation of axial and circumferential cracks, widespread particle breakage, and the formation of inter-granular and trans-granular fractures, as well as shear scratches at the micro level, ultimately manifesting macroscopically as shear-tensile composite failure.</p></div>","PeriodicalId":288,"journal":{"name":"Construction and Building Materials","volume":"449 ","pages":"Article 138264"},"PeriodicalIF":7.4000,"publicationDate":"2024-09-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Construction and Building Materials","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0950061824034068","RegionNum":1,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"CONSTRUCTION & BUILDING TECHNOLOGY","Score":null,"Total":0}
引用次数: 0
Abstract
Significant unloading failure zones in artificial freezing shaft sinking projects in western China are primarily caused by stress release. To investigate the deformation and failure mechanisms of frozen weakly cemented sandstone (FWCS), three groups of triaxial unloading tests were conducted under different initial principal stresses (σ₃ = 3, 6, and 10 MPa) with an unloading rate of 0.05 MPa/s. Scanning electron microscopy (SEM) was employed to examine the micro-fracture characteristics of the failure surfaces. The results revealed that, compared to traditional triaxial and room-temperature triaxial compression tests, the strength and plastic deformation characteristics of FWCS are significantly weakened under unloading conditions. However, lateral deformation, particularly volumetric strain, increased markedly, exhibiting pronounced dilatancy characteristics, especially along stress path III (i.e., post-peak axial stress loading with confining pressure unloading). Unloading leads to a reduction in cohesion and an increase in the internal friction angle of FWCS, with the most significant changes observed along stress path IV (i.e., pre-peak constant axial displacement loading with confining pressure unloading). Macroscopic and microscopic analyses indicate that the failure mechanism of FWCS under complex unloading stress paths is driven by the rapid accumulation of energy caused by unloading, which results in the development and propagation of axial and circumferential cracks, widespread particle breakage, and the formation of inter-granular and trans-granular fractures, as well as shear scratches at the micro level, ultimately manifesting macroscopically as shear-tensile composite failure.
期刊介绍:
Construction and Building Materials offers an international platform for sharing innovative and original research and development in the realm of construction and building materials, along with their practical applications in new projects and repair practices. The journal publishes a diverse array of pioneering research and application papers, detailing laboratory investigations and, to a limited extent, numerical analyses or reports on full-scale projects. Multi-part papers are discouraged.
Additionally, Construction and Building Materials features comprehensive case studies and insightful review articles that contribute to new insights in the field. Our focus is on papers related to construction materials, excluding those on structural engineering, geotechnics, and unbound highway layers. Covered materials and technologies encompass cement, concrete reinforcement, bricks and mortars, additives, corrosion technology, ceramics, timber, steel, polymers, glass fibers, recycled materials, bamboo, rammed earth, non-conventional building materials, bituminous materials, and applications in railway materials.