{"title":"Scratching properties of 4H–SiC single crystal after oxidation under different conditions","authors":"","doi":"10.1016/j.wear.2024.205503","DOIUrl":null,"url":null,"abstract":"<div><p>Single-crystal silicon carbide (SiC) has poor machinability because of its low fracture toughness, and surface modification has become the first choice for SiC polishing to obtain a high removal rate and a smooth surface. However, the removal mechanism of SiC after modification remains unclear. In this study, diamond scratching experiments were performed on 4H–SiC after oxidation under two conditions. To reveal the material removal mechanism, the scratch morphology and subsurface defects were analysed using Raman spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The results showed that oxidation improved the scratch depth and critical depth for ductile removal, resulting in a smooth scratch surface with low damage. However, weak oxidation increased the median crack length and exacerbated the subsurface damage. The SiO<sub>x</sub>C<sub>y</sub>, C = O, C–O–C, and Si–O–Si functional groups produced during oxidation reduced the hardness and improved the machinability of the 4H–SiC substrate. On the other hand, strong oxidation reduced the generation of surface cracks, tearing, and spalling, and weakened the propagation of subsurface median cracks. These results prove that ultrasonic-assisted photocatalytic oxidation provides high removal efficiency and defect control, providing a new approach for the synergistic polishing of SiC substrates.</p></div>","PeriodicalId":23970,"journal":{"name":"Wear","volume":null,"pages":null},"PeriodicalIF":5.3000,"publicationDate":"2024-07-23","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Wear","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0043164824002680","RegionNum":1,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"ENGINEERING, MECHANICAL","Score":null,"Total":0}
引用次数: 0
Abstract
Single-crystal silicon carbide (SiC) has poor machinability because of its low fracture toughness, and surface modification has become the first choice for SiC polishing to obtain a high removal rate and a smooth surface. However, the removal mechanism of SiC after modification remains unclear. In this study, diamond scratching experiments were performed on 4H–SiC after oxidation under two conditions. To reveal the material removal mechanism, the scratch morphology and subsurface defects were analysed using Raman spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The results showed that oxidation improved the scratch depth and critical depth for ductile removal, resulting in a smooth scratch surface with low damage. However, weak oxidation increased the median crack length and exacerbated the subsurface damage. The SiOxCy, C = O, C–O–C, and Si–O–Si functional groups produced during oxidation reduced the hardness and improved the machinability of the 4H–SiC substrate. On the other hand, strong oxidation reduced the generation of surface cracks, tearing, and spalling, and weakened the propagation of subsurface median cracks. These results prove that ultrasonic-assisted photocatalytic oxidation provides high removal efficiency and defect control, providing a new approach for the synergistic polishing of SiC substrates.
期刊介绍:
Wear journal is dedicated to the advancement of basic and applied knowledge concerning the nature of wear of materials. Broadly, topics of interest range from development of fundamental understanding of the mechanisms of wear to innovative solutions to practical engineering problems. Authors of experimental studies are expected to comment on the repeatability of the data, and whenever possible, conduct multiple measurements under similar testing conditions. Further, Wear embraces the highest standards of professional ethics, and the detection of matching content, either in written or graphical form, from other publications by the current authors or by others, may result in rejection.