Dandan Wei, Yulin Huang, Pengfei Ren, Min Liang, Li Xu, Liuxin Yang, Tianzhu Zhang, Zhenling Ji
{"title":"Effect of Compressive Modulus of Porous PVA Hydrogel Coating on the Preventing Adhesion of Polypropylene Mesh","authors":"Dandan Wei, Yulin Huang, Pengfei Ren, Min Liang, Li Xu, Liuxin Yang, Tianzhu Zhang, Zhenling Ji","doi":"10.1002/mabi.202400112","DOIUrl":null,"url":null,"abstract":"<p>PP mesh is a widely used prosthetic material in hernia repair. However, visceral adhesion is one of the worst complications of this operation. Hence, an anti-adhesive PP mesh is developed by coating porous polyvinyl alcohol (PVA) hydrogel on PP surface via freezing-thawing process method. The compressive modulus of porous PVA hydrogel coating is first regulated by the addition of porogen sodium bicarbonate (NaHCO<sub>3</sub>) at various quality ratios with PVA. As expected, the porous hydrogel coating displayed modulus more closely resembling that of native abdominal wall tissue. In vitro tests demonstrate the modified PP mesh show superior coating stability, excellent hemocompatibility, and good cytocompatibility. In vivo experiments illustrate that PP mesh coated by the PVA4 hydrogel that mimicked the modulus of native abdominal wall could prevent adhesion effectively. Based on this, the rapamycin (RPM) is loaded into the porous PVA4 hydrogel coating to further improve anti-adhesive property of PP mesh. The Hematoxylin and eosin (H&E) and Masson trichrome (MT) staining results verified that the resulting mesh could alleviate the inflammation response and reduce the deposition of collagen around the implantation zone. The biomimetic mechanical property and anti-adhesive property of modified PP mesh make it a valuable candidate for application in hernioplasty.</p>","PeriodicalId":18103,"journal":{"name":"Macromolecular bioscience","volume":null,"pages":null},"PeriodicalIF":4.4000,"publicationDate":"2024-06-08","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Macromolecular bioscience","FirstCategoryId":"5","ListUrlMain":"https://onlinelibrary.wiley.com/doi/10.1002/mabi.202400112","RegionNum":4,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"BIOCHEMISTRY & MOLECULAR BIOLOGY","Score":null,"Total":0}
引用次数: 0
Abstract
PP mesh is a widely used prosthetic material in hernia repair. However, visceral adhesion is one of the worst complications of this operation. Hence, an anti-adhesive PP mesh is developed by coating porous polyvinyl alcohol (PVA) hydrogel on PP surface via freezing-thawing process method. The compressive modulus of porous PVA hydrogel coating is first regulated by the addition of porogen sodium bicarbonate (NaHCO3) at various quality ratios with PVA. As expected, the porous hydrogel coating displayed modulus more closely resembling that of native abdominal wall tissue. In vitro tests demonstrate the modified PP mesh show superior coating stability, excellent hemocompatibility, and good cytocompatibility. In vivo experiments illustrate that PP mesh coated by the PVA4 hydrogel that mimicked the modulus of native abdominal wall could prevent adhesion effectively. Based on this, the rapamycin (RPM) is loaded into the porous PVA4 hydrogel coating to further improve anti-adhesive property of PP mesh. The Hematoxylin and eosin (H&E) and Masson trichrome (MT) staining results verified that the resulting mesh could alleviate the inflammation response and reduce the deposition of collagen around the implantation zone. The biomimetic mechanical property and anti-adhesive property of modified PP mesh make it a valuable candidate for application in hernioplasty.
期刊介绍:
Macromolecular Bioscience is a leading journal at the intersection of polymer and materials sciences with life science and medicine. With an Impact Factor of 2.895 (2018 Journal Impact Factor, Journal Citation Reports (Clarivate Analytics, 2019)), it is currently ranked among the top biomaterials and polymer journals.
Macromolecular Bioscience offers an attractive mixture of high-quality Reviews, Feature Articles, Communications, and Full Papers.
With average reviewing times below 30 days, publication times of 2.5 months and listing in all major indices, including Medline, Macromolecular Bioscience is the journal of choice for your best contributions at the intersection of polymer and life sciences.