{"title":"Mechanical and physical properties of splint materials for oral appliances produced by additive, subtractive and conventional manufacturing","authors":"","doi":"10.1016/j.dental.2024.05.030","DOIUrl":null,"url":null,"abstract":"<div><h3>Objectives</h3><p>To investigate the flexural strength (FS), elastic modulus (E), Martens hardness (HM), water sorption (w<sub>sp</sub>), water solubility (w<sub>sl</sub>) and degree of conversion (DC) of 3D-printed, milled and injection molded splint materials.</p></div><div><h3>Methods</h3><p>Specimens (N = 1140) were fabricated from five 3D-printed (GR-22 flex, GR-10 guide, ProArt Print Splint clear, V-Print Splint, V-Print Splint comfort), five milled (BioniCut, EldyPlus, ProArt CAD Splint clear, Temp Premium Flexible, Thermeo) and two injection molded (PalaXPress clear, Pro Base Cold) materials. FS, E, HM, w<sub>sp</sub>, w<sub>sl</sub> and DC were tested initially (24 h, 37 °C, H<sub>2</sub>O), after water storage (90 d, 37 °C, H<sub>2</sub>O) as well as after thermal cycling (5000 thermal cycles, 5/55 °C). Data were analyzed with Kolmogorov-Smirnov, Kruskal- Wallis, Mann-Whitney U test and Spearman’s correlation (p < 0.05).</p></div><div><h3>Results</h3><p>Initially, the mean flexural strength values ranged from 1.9 to 90.7 MPa for printed, 3.8 to 107 MPa for milled and 99.7 to 102 MPa for injection molded materials. The initial mean elastic modulus values were 0.0 to 2.4 GPa for printed, 0.1 to 2.7 GPa for milled and 2.8 GPa for injection molded materials. The initial mean Martens hardness values were 14.5 to 126 N/mm<sup>2</sup> for printed, 50.2 to 171 N/mm<sup>2</sup> for milled and 143 to 151 N/mm<sup>2</sup> for injection molded materials. Initially, the mean water sorption values ranged from 23.1 to 41.2 μg/mm<sup>3</sup> for printed, 4.5 to 23.5 μg/mm<sup>3</sup> for milled and from 22.5 to 23.3 μg/ mm<sup>3</sup> for injection molded materials. The initial mean water solubility values ranged from 2.2 to 7.1 μg/mm<sup>3</sup> for printed, 0.0 to 0.5 μg/mm<sup>3</sup> for milled and 0.1 to 0.3 μg/mm<sup>3</sup> for injection molded materials. After water storage and thermal cycling most of the values decreased and some increased. The mean DC values ranged initially from 72.3 to 94.5 %, after water storage from 74.2 to 96.8 % and after thermal cycling from 75.6 to 95.4 % for the printed materials.</p></div><div><h3>Significance</h3><p>The mechanical and physical properties of printed, milled and injection molded materials for occlusal devices vary and are influenced by aging processes. For clinical applications, materials need to be chosen according to the specific indications.</p></div>","PeriodicalId":298,"journal":{"name":"Dental Materials","volume":null,"pages":null},"PeriodicalIF":4.6000,"publicationDate":"2024-06-08","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S0109564124001313/pdfft?md5=65ccc403870cc56766f0d8cc6216252f&pid=1-s2.0-S0109564124001313-main.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Dental Materials","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0109564124001313","RegionNum":1,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
引用次数: 0
Abstract
Objectives
To investigate the flexural strength (FS), elastic modulus (E), Martens hardness (HM), water sorption (wsp), water solubility (wsl) and degree of conversion (DC) of 3D-printed, milled and injection molded splint materials.
Methods
Specimens (N = 1140) were fabricated from five 3D-printed (GR-22 flex, GR-10 guide, ProArt Print Splint clear, V-Print Splint, V-Print Splint comfort), five milled (BioniCut, EldyPlus, ProArt CAD Splint clear, Temp Premium Flexible, Thermeo) and two injection molded (PalaXPress clear, Pro Base Cold) materials. FS, E, HM, wsp, wsl and DC were tested initially (24 h, 37 °C, H2O), after water storage (90 d, 37 °C, H2O) as well as after thermal cycling (5000 thermal cycles, 5/55 °C). Data were analyzed with Kolmogorov-Smirnov, Kruskal- Wallis, Mann-Whitney U test and Spearman’s correlation (p < 0.05).
Results
Initially, the mean flexural strength values ranged from 1.9 to 90.7 MPa for printed, 3.8 to 107 MPa for milled and 99.7 to 102 MPa for injection molded materials. The initial mean elastic modulus values were 0.0 to 2.4 GPa for printed, 0.1 to 2.7 GPa for milled and 2.8 GPa for injection molded materials. The initial mean Martens hardness values were 14.5 to 126 N/mm2 for printed, 50.2 to 171 N/mm2 for milled and 143 to 151 N/mm2 for injection molded materials. Initially, the mean water sorption values ranged from 23.1 to 41.2 μg/mm3 for printed, 4.5 to 23.5 μg/mm3 for milled and from 22.5 to 23.3 μg/ mm3 for injection molded materials. The initial mean water solubility values ranged from 2.2 to 7.1 μg/mm3 for printed, 0.0 to 0.5 μg/mm3 for milled and 0.1 to 0.3 μg/mm3 for injection molded materials. After water storage and thermal cycling most of the values decreased and some increased. The mean DC values ranged initially from 72.3 to 94.5 %, after water storage from 74.2 to 96.8 % and after thermal cycling from 75.6 to 95.4 % for the printed materials.
Significance
The mechanical and physical properties of printed, milled and injection molded materials for occlusal devices vary and are influenced by aging processes. For clinical applications, materials need to be chosen according to the specific indications.
期刊介绍:
Dental Materials publishes original research, review articles, and short communications.
Academy of Dental Materials members click here to register for free access to Dental Materials online.
The principal aim of Dental Materials is to promote rapid communication of scientific information between academia, industry, and the dental practitioner. Original Manuscripts on clinical and laboratory research of basic and applied character which focus on the properties or performance of dental materials or the reaction of host tissues to materials are given priority publication. Other acceptable topics include application technology in clinical dentistry and dental laboratory technology.
Comprehensive reviews and editorial commentaries on pertinent subjects will be considered.