{"title":"Sintering of Amorphous Al(OH)3 Using Cold Isostatic Pressing","authors":"S. Yu. Prilipko, G. K. Volkova, L. V. Loladze, I. I. Bryukhanova, G. N. Golovan, V. A. Glazunova","doi":"10.1007/s10717-024-00645-6","DOIUrl":null,"url":null,"abstract":"<p>It was found that the high decomposition temperature of amorphous Al(OH)<sub>3</sub> makes it possible to sinter corundum ceramics directly from aluminum hydroxide, bypassing the stage of its preliminary thermal dehydration. Using the cold isostatic pressing method at 200, 600, and 1000 MPa, compacts with densities of 62, 69, and 79% of the theoretical value were obtained. The temperature dependence of the shrinkage of amorphous Al(OH)<sub>3</sub> compacts was studied as a function of the cold isostatic pressing pressure. An area of intense shrinkage was discovered in the range 1050 – 1150°C, which coincides with both the temperature of complete decomposition of amorphous Al(OH)<sub>3</sub> and the transition γ → α-Al<sub>2</sub>O<sub>3</sub>.</p>","PeriodicalId":579,"journal":{"name":"Glass and Ceramics","volume":"80 11-12","pages":"521 - 523"},"PeriodicalIF":0.6000,"publicationDate":"2024-04-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Glass and Ceramics","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s10717-024-00645-6","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}
引用次数: 0
Abstract
It was found that the high decomposition temperature of amorphous Al(OH)3 makes it possible to sinter corundum ceramics directly from aluminum hydroxide, bypassing the stage of its preliminary thermal dehydration. Using the cold isostatic pressing method at 200, 600, and 1000 MPa, compacts with densities of 62, 69, and 79% of the theoretical value were obtained. The temperature dependence of the shrinkage of amorphous Al(OH)3 compacts was studied as a function of the cold isostatic pressing pressure. An area of intense shrinkage was discovered in the range 1050 – 1150°C, which coincides with both the temperature of complete decomposition of amorphous Al(OH)3 and the transition γ → α-Al2O3.
期刊介绍：
Glass and Ceramics reports on advances in basic and applied research and plant production techniques in glass and ceramics. The journal''s broad coverage includes developments in the areas of silicate chemistry, mineralogy and metallurgy, crystal chemistry, solid state reactions, raw materials, phase equilibria, reaction kinetics, physicochemical analysis, physics of dielectrics, and refractories, among others.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号