Microstructure and properties of hypereutectic high chromium cast iron containing nitrogen

IF 1.7 4区材料科学 Q3 MATERIALS SCIENCE, MULTIDISCIPLINARY

Materials Science and Technology Pub Date : 2024-01-01 DOI:10.1177/02670836231212611

Liu Yawei, Liqiang Gong, Dong Minqi, Zhengyang Chen, Tounan Jin, Wenhang Yin, Hanguang Fu

引用次数: 0

Abstract

This article investigates the effect of N content on the microstructure, mechanical properties and wear resistance of hypereutectic high chromium cast iron (HHCCI). With the increase of N content, the primary carbides are obviously refined, the austenite content increases, and the dispersed granular Cr2N precipitates. After quenching at 1000 °C, secondary carbides are precipitated from the matrix, the matrix transforms into martensite + retained austenite. With the increase of N content, the corrosion resistance of HHCCI increases, and 0.3 wt.% N HHCCI shows the best corrosion resistance. With the increase of N content, the wear resistance of HHCCI increases. The wear resistance of HHCCI with 0.15 wt.% N is the best, which is 1.57 times that of HHCCI without N.

查看原文本刊更多论文

含氮过共晶高铬铸铁的显微组织和性能

本文研究了氮含量对超共晶高铬铸铁（HHCCI）的显微组织、力学性能和耐磨性的影响。随着 N 含量的增加，一次碳化物明显细化，奥氏体含量增加，并析出分散的粒状 Cr2N。1000 °C 淬火后，二次碳化物从基体中析出，基体转变为马氏体+残余奥氏体。随着 N 含量的增加，HHCCI 的耐腐蚀性增强，0.3 wt.% N HHCCI 的耐腐蚀性最好。随着 N 含量的增加，HHCCI 的耐磨性也随之增加。含 0.15 wt.% N 的 HHCCI 的耐磨性最好，是不含 N 的 HHCCI 的 1.57 倍。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文求助全文

来源期刊

Materials Science and Technology 工程技术-材料科学：综合

CiteScore

2.70

自引率

5.60%

发文量

审稿时长

3 months

期刊介绍：《Materials Science and Technology》（MST） is an international forum for the publication of refereed contributions covering fundamental and technological aspects of materials science and engineering.