Karakterisasi Nanoselulosa dari Tandan Kosong Aren (Arenga pinnata) sebagai Filler dalam Pembuatan Tisu

Jurnal Sains dan Kesehatan Pub Date : 2024-02-29 DOI:10.25026/jsk.v6i1.2156

Widhi Mulya Nurdin, Irmawati Irmawati, La Ode Muhamad Alwan, Haeruddin Haeruddin

{"title":"Karakterisasi Nanoselulosa dari Tandan Kosong Aren (Arenga pinnata) sebagai Filler dalam Pembuatan Tisu","authors":"Widhi Mulya Nurdin, Irmawati Irmawati, La Ode Muhamad Alwan, Haeruddin Haeruddin","doi":"10.25026/jsk.v6i1.2156","DOIUrl":null,"url":null,"abstract":"The high demand for tissue made from wood as the main raw material has led to the shrinkage of Indonesian forests. Nanocellulose from empty palm bunches was prepared in this study by delignification, hydrolysis and ultrasonication in order to obtain the optimum ultrasonification time. Time variations were 15 min, 30 min and 45 min at 50°C. FTIR analysis showed wavelengths for ?-cellulose functional groups of empty palm bunches, namely O-H groups at 3042.43 cm-1, C-H at 2900.94 cm-1 and C-O at 1049.28cm-1. FE-SEM analysis showed that nanocellulose with 45 min ultrasonification time has a particle size that meets the criteria of nanoparticles. The addition of nanocellulose in napkins increased the thickness and water absorption, with the addition of 6 g of nanocellulose giving the most significant results. With further research, the utilization of TKA in the tissue industry can help to reduce pressure on forests and provide a sustainable alternative for tissue production.\nKeywords: Nanocellulose, Aren Empty Bunch, Filler\n \nAbstrak\nTingginya permintaan tisu yang terbuat dari kayu sebagai bahan baku utamanya telah menyebabkan penyusutan hutan Indonesia. Nanoselulosa tandan kosong aren dibuat dalam penelitian ini melalui proses delignifikasi, hidrolisis dan ultrasonifiasi dengan tujuan untu mendapatkan waktu ultrasonifikasi yang optimum. Metode penelitian yang digunakan meliputi proses delignifikasi, hidrolisis asam serta ultrasonifikasi. Variasi waktu yang dilakukan 15 menit, 30 menit dan 45 menit pada suhu 50oC. Hasil analisis FTIR menunjukkan panjang gelombang untuk gugus fungsi ?-selulosa tandan kosong aren yaitu gugus O-H pada daerah 3042,43 cm-1, C-H pada 2900,94 cm-1 dan C-O 1049,28cm-1 . Hasil analisis FE-SEM menunjukkan bahwa nanoselulosa dengan lama waktu ultrasonifikasi 45 menit memiliki ukuran partikel yang memenuhi kriteria nanopartikel. Penambahan nanoselulosa dalam tisu napkins meningkatkan ketebalan dan daya serap air, dengan penambahan 6 gr nanoselulosa memberikan hasil yang paling signifikan. Dengan penelitian lebih lanjut, pemanfaatan TKA dalam industri tisu dapat membantu mengurangi tekanan terhadap hutan dan menyediakan alternatif yang berkelanjutan untuk produksi tisu.\nKata Kunci: Nanoselulosa, Tandan Kosong Aren, Filler","PeriodicalId":473028,"journal":{"name":"Jurnal Sains dan Kesehatan","volume":"77 2","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2024-02-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Jurnal Sains dan Kesehatan","FirstCategoryId":"0","ListUrlMain":"https://doi.org/10.25026/jsk.v6i1.2156","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

The high demand for tissue made from wood as the main raw material has led to the shrinkage of Indonesian forests. Nanocellulose from empty palm bunches was prepared in this study by delignification, hydrolysis and ultrasonication in order to obtain the optimum ultrasonification time. Time variations were 15 min, 30 min and 45 min at 50°C. FTIR analysis showed wavelengths for ?-cellulose functional groups of empty palm bunches, namely O-H groups at 3042.43 cm-1, C-H at 2900.94 cm-1 and C-O at 1049.28cm-1. FE-SEM analysis showed that nanocellulose with 45 min ultrasonification time has a particle size that meets the criteria of nanoparticles. The addition of nanocellulose in napkins increased the thickness and water absorption, with the addition of 6 g of nanocellulose giving the most significant results. With further research, the utilization of TKA in the tissue industry can help to reduce pressure on forests and provide a sustainable alternative for tissue production. Keywords: Nanocellulose, Aren Empty Bunch, Filler Abstrak Tingginya permintaan tisu yang terbuat dari kayu sebagai bahan baku utamanya telah menyebabkan penyusutan hutan Indonesia. Nanoselulosa tandan kosong aren dibuat dalam penelitian ini melalui proses delignifikasi, hidrolisis dan ultrasonifiasi dengan tujuan untu mendapatkan waktu ultrasonifikasi yang optimum. Metode penelitian yang digunakan meliputi proses delignifikasi, hidrolisis asam serta ultrasonifikasi. Variasi waktu yang dilakukan 15 menit, 30 menit dan 45 menit pada suhu 50oC. Hasil analisis FTIR menunjukkan panjang gelombang untuk gugus fungsi ?-selulosa tandan kosong aren yaitu gugus O-H pada daerah 3042,43 cm-1, C-H pada 2900,94 cm-1 dan C-O 1049,28cm-1 . Hasil analisis FE-SEM menunjukkan bahwa nanoselulosa dengan lama waktu ultrasonifikasi 45 menit memiliki ukuran partikel yang memenuhi kriteria nanopartikel. Penambahan nanoselulosa dalam tisu napkins meningkatkan ketebalan dan daya serap air, dengan penambahan 6 gr nanoselulosa memberikan hasil yang paling signifikan. Dengan penelitian lebih lanjut, pemanfaatan TKA dalam industri tisu dapat membantu mengurangi tekanan terhadap hutan dan menyediakan alternatif yang berkelanjutan untuk produksi tisu. Kata Kunci: Nanoselulosa, Tandan Kosong Aren, Filler

查看原文本刊更多论文

将空束阿伦（桄榔）中的纳米纤维素作为组织制造中的填充物的特性分析

对以木材为主要原料制成的纸巾的需求量很大，导致印度尼西亚森林面积缩小。本研究通过木质素脱除、水解和超声波处理来制备空棕榈果穗的纳米纤维素，以获得最佳超声波处理时间。时间变化为 15 分钟、30 分钟和 45 分钟，温度为 50°C。傅立叶变换红外光谱分析显示了空棕榈果穗纤维素官能团的波长，即 O-H 在 3042.43 厘米-1，C-H 在 2900.94 厘米-1，C-O 在 1049.28 厘米-1。FE-SEM 分析表明，超声时间为 45 分钟的纳米纤维素的粒径符合纳米颗粒的标准。在餐巾纸中添加纳米纤维素可增加餐巾纸的厚度和吸水性，其中添加 6 克纳米纤维素的效果最为显著。随着研究的深入，在卫生纸行业中利用 TKA 有助于减轻对森林的压力，并为卫生纸生产提供一种可持续的替代品：纳米纤维素、Aren 空束、填料摘要对以木材为主要原料的卫生纸的高需求导致了印度尼西亚森林的萎缩。本研究通过脱木质素、水解和超声波处理制备了阿伦空束纳米纤维素，目的是获得最佳的超声波处理时间。研究方法包括脱木质素、酸水解和超声波处理。时间变化为 15 分钟、30 分钟和 45 分钟，温度为 50 摄氏度。傅立叶变换红外光谱分析显示了空棕榈果穗纤维素的官能团波长，即 O-H 在 3042.43 厘米-1，C-H 在 2900.94 厘米-1，C-O 在 1049.28 厘米-1。FE-SEM 分析表明，超声时间为 45 分钟的纳米纤维素的粒径符合纳米颗粒的标准。在餐巾纸中添加纳米纤维素可增加厚度和吸水性，其中添加 6 克纳米纤维素的效果最为显著。随着研究的深入，在卫生纸行业中利用 TKA 有助于减轻对森林的压力，并为卫生纸生产提供一种可持续的替代品：纳米纤维素空果束填充物