Comparison of conjunctival pedicle flap to corneal fixation strength achieved by Tisseel® fibrin glue, ethyl cyanoacrylate adhesive, ReSure® hydrogel sealant, and conventional suturing with 8-0 VICRYL® ophthalmic suture.

Abstract

Objective: To determine and compare the fixation strength of conjunctival pedicle flaps to cornea achieved via conventional ophthalmic suture and three different adhesive compounds.

Animals studied: Ex vivo porcine globes.

Procedures: Following a 6 mm wide 500-micron-restricted depth lamellar keratectomy, conjunctival pedicle flaps were secured to the keratectomy site with either 8-0 VICRYL® suture or one of three adhesive products, including Tisseel® bioadhesive, ReSure® synthetic adhesive, or ethyl cyanoacrylate adhesive (n = 10 per surgical group). Adhesive application protocol varied by product based upon adhesive biocompatibility. Corneoconjunctival tissues were then harvested, clamped in a tensile testing device, and loaded at a rate of 1 mm/s under video surveillance until the point of failure. Peak load was determined for each test and used to compare fixation strength between samples.

Results: Forty conjunctival flaps were performed, with 6 omitted from evaluation due to dehiscence prior to tensile testing. Of the 34 flaps analyzed, 10 were secured with suture, 10 with cyanoacrylate, 8 with ReSure®, and 6 with Tisseel®. Flaps secured with suture withstood significantly higher applied tensile force compared with cyanoacrylate (p = .02474), ReSure® (p = .00000), and Tisseel® (p = .00002). Flaps secured with cyanoacrylate withstood significantly greater force than those secured with ReSure® and Tisseel® (p = .01194 and 0.01798, respectively). There was no significant difference in fixation strength between ReSure® and Tisseel® glue (p = .95675).

Conclusions: Conjunctival pedicle flap fixation using 8-0 VICRYL® suture fixation was able to withstand significantly greater maximum tensile force compared to ReSure®, Tisseel®, or cyanoacrylate adhesives. Fixation strength achieved with cyanoacrylate adhesive was significantly greater than that achieved with ReSure® or Tisseel®.