[Bond strength of metal brackets to enamel with a Russian adhesive complex: an in vitro study].

Abstract

Background: The era of using adhesives to fix brackets began in the 70s of the last century. There are eight generations of foreign-made adhesive systems for the restoration of teeth. However, until now, in orthodontics, the development of domestic adhesive systems with improved properties of adhesion of brackets to tooth enamel still important, especially in the posterior teeth.

Objective: The purpose of this work was to study the shear strength of fifth generation domestic adhesive between metal brackets and the enamel of molar teeth in laboratory conditions.

Material and methods: The study included 17 specimens of extracted maxillary molars embedded in acrylic resin blocks. Brackets from G&H Orthodontics (G&H Wire Company, USA) were fixed to the tooth enamel using the domestic Compofix (ortho) set. The enamel was treated with etching gel (37% phosphoric acid) for 30 seconds. Then the gel was washed off with water and the surface of the enamel was thoroughly dried. A primer was applied to the prepared surface with an applicator, inflated with a weak air flow for 5-10 seconds and photopolymerized for 20 seconds. The surface of the bracket was treated with degreaser, then a thin layer of adhesive was applied, and the sample was fixed to the enamel. Excess material was removed with an applicator. The samples were photopolymerized for 20 sec. Then, the shear bond strength of the adhesive was determined according to the method of GOST 31574-2012 on a (Zwick/Roell Z010 testing machine, Zwick, Germany).

Results: The shear strength of the adhesive joint obtained during the test is 13.54±1.01 MPa, the average value of the index of adhesive residues on the surface of the bracket was 23%±4%, which corresponds to the standard average values according to GOST.

Conclusion: The tested domestic adhesive system of the fifth generation can be recommended for the practical work of an orthodontist.