Pengaruh Penambahan Waste Glass sebagai Agregat Kasar terhadap Kuat Tekan Beton

INERSIA lnformasi dan Ekspose Hasil Riset Teknik Sipil dan Arsitektur Pub Date : 2021-12-31 DOI:10.21831/inersia.v17i2.41223

S. Utami, M. Zaini, Adib Wajyu Hidayat

{"title":"Pengaruh Penambahan Waste Glass sebagai Agregat Kasar terhadap Kuat Tekan Beton","authors":"S. Utami, M. Zaini, Adib Wajyu Hidayat","doi":"10.21831/inersia.v17i2.41223","DOIUrl":null,"url":null,"abstract":"ABSTRACTThis research aims to utilize glass waste as the basic material of coarse aggregate in the concrete mix used to reduce glass waste. This research uses 15 specimens with 150 x 300 mm in dimensions. The test results of normal concrete (BN) at 7, 14, and 28 days were 20.95 N/mm, 28.31 N/mm, and 34.54 N/mm. The BWG 1 at 7, 14, and 28 days was 24.35 N/mm, 25.48 N/mm, and 33.97 N/mm. BWG2 at 7, 14, and 28 days of 17.55 N/mm², 23.78 N/mm, and 29.44 N/mm. Waste glass (BWG3) at 7, 14, and 28 days of 20.38 N/mm², 20.95 N/mm, and 26.04 N/mm. BWG4 at 7, 14, and 28 were 13.02 N/mm, 19.82 N/mm, and 22.08 N/mm. Comparison of the compressive strength of normal concrete with waste glass concrete at the age of 7 days showed that BWG1 increased around 16%. As for other test specimens, there was a decrease in compressive strength compared to BN were the results for BW2, BW3, BW4 (16%, 3%, and 38%). At 14 days shows that the BWG1, BWG2, BWG3, and BWG4 decrease by 10%, 16%, 26%, and 30%. At 28 days showed the BWG1, BWG2, BWG3, and BWG4 decrease of 2%, 15%, 25%, and 36% compared to BN. ABSTRAKPenelitian ini bertujuan untuk memanfaatkan limbah kaca sebagai bahan dasar agregat kasar dalam campuran beton yang digunakan untuk mereduksi limbah kaca. Penelitian ini menggunakan 15 benda uji dengan dimensi 150 x 300 mm. Hasil pengujian beton normal (BN) pada umur 7, 14, dan 28 hari adalah 20,95 N/mm, 28,31 N/mm, dan 34,54 N/mm. BWG 1 pada hari ke 7, 14, dan 28 adalah 24,35 N/mm, 25,48 N/mm, dan 33,97 N/mm. BWG 2 pada 7, 14, dan 28 hari sebesar 17,55 N/mm², 23,78 N/mm, dan 29,44 N/mm. BWG 3 pada 7, 14, dan 28 hari sebesar 20,38 N/mm², 20,95 N/mm, dan 26,04 N/mm. BWG 4 pada 7, 14, dan 28 adalah 13,02 N/mm, 19,82 N/mm, dan 22,08 N/mm. Perbandingan kuat tekan beton normal dengan beton limbah kaca pada umur 7 hari menunjukkan bahwa BWG1 meningkat sekitar 16%. Sedangkan untuk benda uji lainnya terjadi penurunan kuat tekan dibandingkan dengan BN yaitu pada hasil BW2, BW3, BW4 (16%, 3%, dan 38%). Pada 14 hari menunjukkan bahwa BWG1, BWG2, BWG3, dan BWG4 mengalami penurunan sebesar 10%, 16%, 26%, dan 30%. Pada hari ke 28 menunjukkan penurunan BWG1, BWG2, BWG3, dan BWG4 sebesar 2%, 15%, 25%, dan 36% dibandingkan dengan BN.","PeriodicalId":425453,"journal":{"name":"INERSIA lnformasi dan Ekspose Hasil Riset Teknik Sipil dan Arsitektur","volume":"2014 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2021-12-31","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"INERSIA lnformasi dan Ekspose Hasil Riset Teknik Sipil dan Arsitektur","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.21831/inersia.v17i2.41223","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

ABSTRACTThis research aims to utilize glass waste as the basic material of coarse aggregate in the concrete mix used to reduce glass waste. This research uses 15 specimens with 150 x 300 mm in dimensions. The test results of normal concrete (BN) at 7, 14, and 28 days were 20.95 N/mm, 28.31 N/mm, and 34.54 N/mm. The BWG 1 at 7, 14, and 28 days was 24.35 N/mm, 25.48 N/mm, and 33.97 N/mm. BWG2 at 7, 14, and 28 days of 17.55 N/mm², 23.78 N/mm, and 29.44 N/mm. Waste glass (BWG3) at 7, 14, and 28 days of 20.38 N/mm², 20.95 N/mm, and 26.04 N/mm. BWG4 at 7, 14, and 28 were 13.02 N/mm, 19.82 N/mm, and 22.08 N/mm. Comparison of the compressive strength of normal concrete with waste glass concrete at the age of 7 days showed that BWG1 increased around 16%. As for other test specimens, there was a decrease in compressive strength compared to BN were the results for BW2, BW3, BW4 (16%, 3%, and 38%). At 14 days shows that the BWG1, BWG2, BWG3, and BWG4 decrease by 10%, 16%, 26%, and 30%. At 28 days showed the BWG1, BWG2, BWG3, and BWG4 decrease of 2%, 15%, 25%, and 36% compared to BN. ABSTRAKPenelitian ini bertujuan untuk memanfaatkan limbah kaca sebagai bahan dasar agregat kasar dalam campuran beton yang digunakan untuk mereduksi limbah kaca. Penelitian ini menggunakan 15 benda uji dengan dimensi 150 x 300 mm. Hasil pengujian beton normal (BN) pada umur 7, 14, dan 28 hari adalah 20,95 N/mm, 28,31 N/mm, dan 34,54 N/mm. BWG 1 pada hari ke 7, 14, dan 28 adalah 24,35 N/mm, 25,48 N/mm, dan 33,97 N/mm. BWG 2 pada 7, 14, dan 28 hari sebesar 17,55 N/mm², 23,78 N/mm, dan 29,44 N/mm. BWG 3 pada 7, 14, dan 28 hari sebesar 20,38 N/mm², 20,95 N/mm, dan 26,04 N/mm. BWG 4 pada 7, 14, dan 28 adalah 13,02 N/mm, 19,82 N/mm, dan 22,08 N/mm. Perbandingan kuat tekan beton normal dengan beton limbah kaca pada umur 7 hari menunjukkan bahwa BWG1 meningkat sekitar 16%. Sedangkan untuk benda uji lainnya terjadi penurunan kuat tekan dibandingkan dengan BN yaitu pada hasil BW2, BW3, BW4 (16%, 3%, dan 38%). Pada 14 hari menunjukkan bahwa BWG1, BWG2, BWG3, dan BWG4 mengalami penurunan sebesar 10%, 16%, 26%, dan 30%. Pada hari ke 28 menunjukkan penurunan BWG1, BWG2, BWG3, dan BWG4 sebesar 2%, 15%, 25%, dan 36% dibandingkan dengan BN.

查看原文本刊更多论文

摘要本研究旨在利用玻璃废料作为混凝土配合比粗骨料的基本原料，以减少玻璃废料。本研究使用15个尺寸为150 × 300毫米的试样。普通混凝土(BN)在7、14、28天的试验结果分别为20.95 N/mm、28.31 N/mm、34.54 N/mm。第7、14和28 d的bwg1分别为24.35 N/mm、25.48 N/mm和33.97 N/mm。在17.55 N/mm²，23.78 N/mm和29.44 N/mm的条件下，BWG2在第7、14和28天。废玻璃(BWG3)在20.38 N/mm²，20.95 N/mm和26.04 N/mm的第7、14和28天。BWG4在7、14、28时分别为13.02 N/mm、19.82 N/mm和22.08 N/mm。普通混凝土与废玻璃混凝土7 d龄期抗压强度对比显示，BWG1增加了16%左右。对于其他试件，BW2、BW3、BW4的抗压强度均比BN有所下降(分别为16%、3%和38%)。14 d时，BWG1、BWG2、BWG3和BWG4分别下降了10%、16%、26%和30%。在第28天，BWG1、BWG2、BWG3和BWG4与BN相比分别下降了2%、15%、25%和36%。摘要:penelitian ini bertujuan untuk manfaatkan limbah kaca sebagai bahan dasar agregat kasar dalam campuran beton yang digunakan untuk mereduksi limbah kaca。Penelitian ini mongunakan 15 benda uji登干尺寸150 x 300 mm。Hasil penguin beton normal (BN)在7月、14日、28日、20日、95 N/mm、28日、31 N/mm、34日、54 N/mm。BWG 1的数据为7、14、28、24、35 N/mm、25、48 N/mm、33、97 N/mm。BWG 2的第7、14、28页，第17、55 N/mm²，第23、78 N/mm，第29、44 N/mm。bwg3、7、14、28、20、38 N/mm²、20、95 N/mm、26、04 N/mm。BWG 4、7、14、28、13、02、19、82、22、08、N/mm。Perbandingan kuat tekan beton normal dengan beton limbah kaca padumur 7 hari menunjukkan bahwa BWG1 meningkat sekitar 16%Sedangkan untuk benda uji lainnya terjadi penurunan kuat tekan dibandingkan dengan BN yitu padhasil BW2, BW3, BW4 (16%， 3%， dan 38%)。Pada 14 hari menunjukkan bahwa BWG1, BWG2, BWG3, dan BWG4 mengalami penurunan sebesar 10%， 16%， 26%， dan 30%。BWG1, BWG2, BWG3, BWG4，分别为2%，15%，25%，36%。