Reliability evaluation of multilevel thin film structures

H. Longworth, E. Perfecto, P. Mclaughlin
{"title":"Reliability evaluation of multilevel thin film structures","authors":"H. Longworth, E. Perfecto, P. Mclaughlin","doi":"10.1109/ECTC.1994.367549","DOIUrl":null,"url":null,"abstract":"IBM Microelectronics has evaluated the reliability of structures built by various processes which we developed for multilevel thin film (MLTF) applications. Two distinct processes were used for the building of conformal copper-polyimide structures on alumina ceramic: Laser ablation of the polyimide for via patterning and wiring defined by subtractive etching of Cr/Cu/Cr, and photosensitive polyimide for via patterning and wiring defined by electroplating through a resist. Reliability evaluation was performed on test-vehicles with both MLTF processes by a combination of IBM standard and MIL-STD-883 stress procedures. These stresses were designed to monitor any potential reliability problems due to metal migration, corrosion (or contamination), metal fatigue, and poor step coverage. Electrical measurements were done before, during, and after stress to check for opens and inter and intralevel shorts. At completion of stressing, no failures were observed in either type of test vehicles. This indicates that both processes meet or exceed IBM current product reliability standards.<<ETX>>","PeriodicalId":344532,"journal":{"name":"1994 Proceedings. 44th Electronic Components and Technology Conference","volume":"28 1 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"1994-05-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"4","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"1994 Proceedings. 44th Electronic Components and Technology Conference","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/ECTC.1994.367549","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 4

Abstract

IBM Microelectronics has evaluated the reliability of structures built by various processes which we developed for multilevel thin film (MLTF) applications. Two distinct processes were used for the building of conformal copper-polyimide structures on alumina ceramic: Laser ablation of the polyimide for via patterning and wiring defined by subtractive etching of Cr/Cu/Cr, and photosensitive polyimide for via patterning and wiring defined by electroplating through a resist. Reliability evaluation was performed on test-vehicles with both MLTF processes by a combination of IBM standard and MIL-STD-883 stress procedures. These stresses were designed to monitor any potential reliability problems due to metal migration, corrosion (or contamination), metal fatigue, and poor step coverage. Electrical measurements were done before, during, and after stress to check for opens and inter and intralevel shorts. At completion of stressing, no failures were observed in either type of test vehicles. This indicates that both processes meet or exceed IBM current product reliability standards.<>
多层薄膜结构的可靠性评估
IBM微电子已经评估了我们为多层薄膜(MLTF)应用开发的各种工艺构建的结构的可靠性。在氧化铝陶瓷上构建共形铜-聚酰亚胺结构采用两种不同的工艺:激光烧蚀聚酰亚胺,通过Cr/Cu/Cr的减法蚀刻形成图案和布线;光敏聚酰亚胺,通过电阻电镀形成图案和布线。通过结合IBM标准和MIL-STD-883应力程序,对两种MLTF工艺的测试车辆进行可靠性评估。这些应力被设计用来监测由于金属迁移、腐蚀(或污染)、金属疲劳和台阶覆盖不足而导致的任何潜在可靠性问题。在应力之前、期间和之后都进行了电气测量,以检查开路、节段间和节段内的短路。在应力完成时,两种类型的试验车辆均未观察到失效。这表明这两个过程都达到或超过了IBM当前的产品可靠性标准。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
自引率
0.00%
发文量
0
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信