ANALISIS KERUSAKAN POROS GENERATOR PEMBANGKIT LISTRIK = DAMAGE ANALYSIS OF A POWER GENERATOR SHAFT

Material Komponen dan Konstruksi Pub Date : 2019-01-09 DOI:10.29122/MKK.V14I2.1661

SA Soedardjo, Y BambangPurnomo

{"title":"ANALISIS KERUSAKAN POROS GENERATOR PEMBANGKIT LISTRIK = DAMAGE ANALYSIS OF A POWER GENERATOR SHAFT","authors":"SA Soedardjo, Y BambangPurnomo","doi":"10.29122/MKK.V14I2.1661","DOIUrl":null,"url":null,"abstract":"The damage shafts of a power generator have analyzed. The background of this analysis is the shaft generators for electricity in Indonesia frequently are broken. The purpose of the analysis is to determine the cause of damage to the shaft generators. Methodologies used include interviews with the owners and employees at the site, visual inspection on site, visual inspection at the workshop, the workshop hardness testing, chemical composition in the laboratory and analysis based on several references. Analysis of the results obtained are: generator shaft number 1A fracture due to rotation overload, shaft number 1B is cracked circular in the fillet, shaft number 2 cracks oriented at an angle of about 45° to the axis of the shaft. The conclusion that can be taken, power generator shaft fractures due to the design of the fillets as a stress concentration is not perfect, excessive loads, and occurred material ductile fracture.Keywords : Shaft, power generator, hardness testing, chemical composationAbstrak Telah dianalisis kerusakan beberapa poros dari suatu generatorpembangkit listrik. Latar belakang analisis ini adalah seringnya terjadi poros generator pembangkit listrik di Indonesia yang patah. Tujuan dari analisis adalah untuk mengetahui penyebab kerusakan poros generator pembangkit listrik. Metodologi yang digunakan antara lain wawancara dengan pemilik dan karyawan di lokasi, pemeriksaan visual di situs, pemeriksaan visual di bengkel, uji kekerasan di bengkel, komposisi kimia di laboratorium dan analisis berdasarkan beberapa referensi. Hasil Analisis yang diperoleh adalah: poros generator nomor 1A patah karena terjadi kelebihan beban putaran, poros nomor 1B retak melingkar di daerah fillet, poros nomor 2 retak yang berorientasi pada sudut sekitar 45° terhadap sumbu poros. Kesimpulan yang dapat diambil, poros generator pembangkit listrik patah karena desain fillet sebagai sumber tegangan yang tidak sempurna, beban berlebihan, dan material mengalami patah ulet.Kata Kunci : poros, pembangkit listrik,uji kekerasan,komposisi kimia","PeriodicalId":398388,"journal":{"name":"Material Komponen dan Konstruksi","volume":"1 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2019-01-09","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Material Komponen dan Konstruksi","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.29122/MKK.V14I2.1661","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

The damage shafts of a power generator have analyzed. The background of this analysis is the shaft generators for electricity in Indonesia frequently are broken. The purpose of the analysis is to determine the cause of damage to the shaft generators. Methodologies used include interviews with the owners and employees at the site, visual inspection on site, visual inspection at the workshop, the workshop hardness testing, chemical composition in the laboratory and analysis based on several references. Analysis of the results obtained are: generator shaft number 1A fracture due to rotation overload, shaft number 1B is cracked circular in the fillet, shaft number 2 cracks oriented at an angle of about 45° to the axis of the shaft. The conclusion that can be taken, power generator shaft fractures due to the design of the fillets as a stress concentration is not perfect, excessive loads, and occurred material ductile fracture.Keywords : Shaft, power generator, hardness testing, chemical composationAbstrak Telah dianalisis kerusakan beberapa poros dari suatu generatorpembangkit listrik. Latar belakang analisis ini adalah seringnya terjadi poros generator pembangkit listrik di Indonesia yang patah. Tujuan dari analisis adalah untuk mengetahui penyebab kerusakan poros generator pembangkit listrik. Metodologi yang digunakan antara lain wawancara dengan pemilik dan karyawan di lokasi, pemeriksaan visual di situs, pemeriksaan visual di bengkel, uji kekerasan di bengkel, komposisi kimia di laboratorium dan analisis berdasarkan beberapa referensi. Hasil Analisis yang diperoleh adalah: poros generator nomor 1A patah karena terjadi kelebihan beban putaran, poros nomor 1B retak melingkar di daerah fillet, poros nomor 2 retak yang berorientasi pada sudut sekitar 45° terhadap sumbu poros. Kesimpulan yang dapat diambil, poros generator pembangkit listrik patah karena desain fillet sebagai sumber tegangan yang tidak sempurna, beban berlebihan, dan material mengalami patah ulet.Kata Kunci : poros, pembangkit listrik,uji kekerasan,komposisi kimia

查看原文本刊更多论文

发电机轴的损伤分析

分析了某发电机轴的损坏情况。这一分析的背景是印度尼西亚的发电轴发电机经常发生故障。分析的目的是确定轴向发电机损坏的原因。使用的方法包括在现场与业主和员工面谈，现场目视检查，车间目视检查，车间硬度测试，实验室化学成分和基于一些参考资料的分析。分析得到的结果是:发电机1A号轴因旋转过载而断裂，1B号轴在圆角处呈圆形裂纹，2号轴的裂纹方向与轴轴线成45°角左右。由此可以得出结论，发电机轴断裂是由于设计时圆角作为应力集中不完善，载荷过大，而发生材料韧性断裂。关键词:轴，发电机，硬度测试，化学成分Latar belakang分析ini adalah seringnya terjadi poros generator pembangkit listrik di Indonesia yang patah。Tujuan dari分析adalah untuk mengetahui penyebab kerusakan poros生成器pembangkit listk。metoological yang digunakan antara lain wawananca dengan penilik dan karyawan di lokasi, permeriksaan visual di siti, permeriksaan visual di bengkel, uji kekerasan di bengkel, komposisi kimia di laboratorium dan analysis berdasarkan beberapa referensi。Hasil分析yang diperoleh adalah: poros generator nomor 1A pathah karena terjadi kelelebihan beban putaran, poros nomor 1B retak melingkar di daerah fillet, poros nomor 2 retak yang berorientasi padsudut sekitar 45°terhadap sumbu poros。kespulpan yang dapat diambil, poros generator pembangkit listrik patah karena desain fillet sebagai sumber tegangan yang tidak sempurna, beban berlebihan, dan material mengalami patah ulet。Kata Kunci: poros, pembangkit listrik,uji kekerasan,komposisi kimia